Evaluation of crack growth rates and microstructures near the crack tip of neutron-irradiated austenitic stainless steels in simulated BWR environment

Chimi, Yasuhiro; Kasahara, Shigeki; Seto, Hitoshi*; Kitsunai, Yuji*; Koshiishi, Masato*; Nishiyama, Yutaka

Proceedings of the 18th International Conference on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Vol.2, p.1039 - 1054, 2018/00

https://doi.org/10.1007/978-3-319-68454-3_76

In order to understand irradiation-assisted stress corrosion cracking (IASCC) growth behavior, crack growth rate (CGR) tests have been performed in simulated Boiling Water Reactor water conditions at 288C on neutron-irradiated 316L stainless steels (SSs) at 12-14 dpa. After the tests, the microstructures near the crack tip of the specimens are examined with scanning transmission electron microscope (FE-STEM). In comparison with a previous study at 2 dpa, this result shows a less benefit of low electrochemical corrosion potential (ECP) conditions on CGR. A crack tip immersed over 1000 hours was filled with oxides, while almost no oxide film was observed near the crack front in the low-ECP conditions. In addition, a high density of deformation twins and dislocations were found near the fracture surface of the crack front. It is considered that both localized deformation and oxidation are possible dominant factors for the SCC growth in highly irradiated SSs.