Microstructural development and radiation hardening of neutron irradiated Mo-Re alloys

Nemoto, Yoshiyuki; Hasegawa, Akira*; Sato, Manabu*; Abe, Katsunori*; Hiraoka, Yutaka*

In this study, stress-relieved specimens and recrystallized specimens of pure Mo and Mo-Re alloys (Re content=2,4,5,10,13 and 41wt%) were neutron irradiated up to 20dpa at various temperatures (681-1072K). On microstructure observation, sigma phase and chi phase precipitates were observed in all irradiated Mo-Re alloys. Voids were observed in all irradiated specimen, and dislocation loops and dislocations were observed in the specimens that were irradiated at lower temperatures. On Vickers hardness testing, all of the irradiated specimens showed hardening. Especially Mo-41Re were drastically embrittled after irradiation at 874K or less. From these results, authors discuss about relation between microstructure development and radiation hardening, embrittlement, and propose the most efficient Re content and thermal treatment for Mo-Re alloys to be used under irradiation condition.

Accesses

:

- Accesses

InCites™

:

Percentile:10.08

Category:Materials Science, Multidisciplinary

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.