Effects of irradiation on mechanical properties of HIP-bonded reduced-activation ferritic/martensitic steel F82H first wall

Furuya, Kazuyuki; Wakai, Eiichi; Miyamoto, Kenji*; Akiba, Masato; Sugimoto, Masayoshi

A partial mock-up of a breeding blanket structure made of F82H steel has been successfully fabricated. In this study, microstructural observation and EDX analysis of the HIP interfaces were performed, and effects of irradiation on mechanical properties of the HIP-bonded region were also examined. Neutron irradiation was performed up to about 2 dpa at about 523 K. After the irradiation, tensile test was performed at temperatures of 295 and 523 K. The HIP interfaces possessed many precipitates, and enriched peak spectrum of chromium was detected from the precipitates. In addition, aspect of the spectrum was qualitatively equivalent to that of M$$_{23}$$C$$_{6}$$ in grain boundaries of F82H steel. In result, the HIP boundary has many M$$_{23}$$C$$_{6}$$ which were generally seen in grain boundaries of F82H steel. Rupture did not occur in the HIP interface. In result, it can be mentioned that bondability is maintained under the irradiation and testing conditions. The strength and elongation of the HIP-bonded region decreased somewhat in comparison with the results of an IEA standard steel.

Accesses

:

- Accesses

InCites™

:

Percentile:100

Category:Materials Science, Multidisciplinary

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.