Mechanical properties on high Cr-Mo steels at elevated temperature (III); Creep properties of high Cr-Mo steel forgings (250$$sim$$280mm t)

not registered; not registered ; Yoshida, Eiichi; not registered

This stady was performed in order to confirm the influence of sampling method on Creep properties of 9Cr-Mo steel forgings which are promising as candidate materials for steam generator of large scale fast breeder reactor. This results are to be reflected on fundation of materials strength standard. Test materials are four kinds of 9Cr-Mo steel forgings (thickness:250$$sim$$280mmt) such as Mod.9Cr-1Mo (F4, F8 heats), 9Cr-1Mo-Nb-V(G3 heat), 9Cr-2Mo (H6 heat) steels. Results obtained are summarized as follows. (1)In order to evaluation of fundamental material properties, creep-rupture data on three kinds of 9Cr-Mo steel forgings such as Mod.9Cr-1Mo, 9Cr-2Mo and 9Cr-1Mo-Nb-V steels was obtained up to 10,000 hours. (2)The Mod.9Cr-1Mo steel exhibited most excellent creep-rupture strength and the 9Cr-2Mo steel was the worst among the three. (3)The effect of the sampling location of specimens on creep strength was not significant for Mod.9Cr-1Mo steel. But for 9Cr-1Mo-Nb-V steel and 9Cr-2Mo steel, longer creep rupture time was observed with spcimens taken from just below the center of the surface with direction of L, and shorter creep rupture time was observed for those taken from t/2 thickness at the center with direction of Z. (4)Creep strength of 9Cr-2Mo steel was lower than that of Mod.9Cr-1Mo (F4, F8)and 9Cr-1Mo-Nb-V steel. But rupture elongation and reduction of area of 9Cr-2Mo steel was greater than hat of other three materials, irrespective of the sampling location of specimens.

Acecsses

:

- Accesses

InCites™

:

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.