lnvestigation for corrosion behavior of ferritic core materials in C0$$_{2}$$ gas cooled reactor

not registered; not registered; Mizuta, Shunji

The corrosion behavior of ferritic stainless steels applied to core components under C0$$_{2}$$ gas environment was investigated in order to be helpful to fuel design in C0$$_{2}$$ gas cooled reactor as the feasibility study for fast breeder reactor. The dependence of the corrosion behavior, before a breakaway occurs, on C0$$_{2}$$ gas temperature, Si and Cr contents of ferritic steels was determined quantitatively. The following correlations to calculate the metal loss thickness was established. X = 4.4w w = √(k$$times$$t) k = $$alpha$$ $$times$$ exp( - 5.45[Si]) $$times$$ exp( - 1.09[Cr]) $$times$$ exp( - 11253/T) $$alpha$$ = 1.65 $$times$$ 10$$^{8}$$$$sim$$4.40 $$times$$ 10$$^{9}$$ X : metal loss thickness[$$mu$$ml, w : corrosion weight gain [mg/cm$$^{2}$$] k : parabola constant [(mg/cm$$^{2}$$)$$^{2}$$/hr], t : time [hr], $$alpha$$ : constant [Si] : Si content[wt.%], [Cr] : Cr content [wt.%], T : temperature [K]

Acecsses

:

- Accesses

InCites™

:

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.