Influence of microstructure on IASCC growth behavior of neutron irradiated type 304 austenitic stainless steels in simulated BWR condition

Kaji, Yoshiyuki  ; Miwa, Yukio; Shibata, Akira ; Nakano, Junichi; Tsukada, Takashi ; Takakura, Kenichi*; Nakata, Kiyotomo*

The CGR tests of neutron irradiated Type 304 SS were conducted in BWR conditions and the results were compared with those of Type 304L and 316L SS, and following results were obtained. (1) The CGR increase with increasing neutron fluence and the power law of K on the CGR was observed above F2 neutron fluence level (1.4 dpa). The different tendency is observed between Type 304 SS and L-grade SS (Type 304L and 316L SS) with increasing neutron fluence above F3 (4.3 dpa) level. (2) The CGR of Type 304 SS is slightly small as compared with those of Type 304L and 316L SS at the same neutron fluence and shows an increasing tendency above 4 dpa and reaches to 1.010m/s in 9 dpa. (3) The neutron fluence dependence on uniform elongation is different with Type 304, 304L SS and Type 316L SS, that is, the neutron fluence in which the local deformation like channeling deformation is dominant, is high for Type 316L SS.