Performance evaluation of friction welded joint of zircaloy-2 to type 316L stainless steel

Kitagishi, Shigeru  ; Saito, Takashi; Kikuchi, Taiji; Endo, Yasuichi; Tsuchiya, Kunihiko 

The development of the friction welded joint between Zircaloy-2 (Zry-2) and Type 316L stainless steel (SUS316L) has been carried out for the fabrication of fuel irradiation capsules in Japan Materials Testing Reactor (JMTR). The welding condition was determined from the fabrication test results of total loss and tensile strength. The joint interface was characterized by metallographic observation, elemental analysis and micro-hardness test. It was found that heat-affected zones at the joint interface were different between the center and outside positions. The tensile strength of the joint was equal to that of base Zry-2 metals at 300$$^{circ}$$C. And, the joint performance was good from the results of helium leak test and hydraulic pressure burst test. From the results of these tests, it was obvious that the Zry-2/SUS316L friction welded joints were promised to use for the structural material of irradiation capsules for fuel irradiation tests.

Accesses

:

- Accesses

InCites™

:

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.