Creep-fatigue evaluation of a structural model made of Mod.9Cr-1Mo steel subjected to the cyclic thermal loading

Ando, Masanori ; Hasebe, Shinichi; Kobayashi, Sumio; Kasahara, Naoto*; Toyoshi, Akira*; Omae, Takahiro*; Enuma, Yasuhiro*

To validate the failure mode and assess creep-fatigue damage evaluation, a thick cylinder test model made of Mod.9Cr-1Mo steel was subjected to 1,873 cycles of accelerated thermal transient loading using a large-scale sodium loop through which liquid sodium at 600C and 250C flowed repeatedly, with the period of each transient being 2 h and 1 h, respectively. After completion of the test, liquid penetrant testing, a surface observation and hardness testing were performed to characterize failure mode. Based on the finite element analysis, creep-fatigue life was evaluated by applying the JSME FRs code. The failure cycles evaluated by rules described in the JSME FRs code was shown to have a safety margin of greater than 300 times for this system.