-edge jump and shift on white-line of Pd interlayer for trilaminar neutron production target under H irradiation

Ishiyama, Shintaro; Fujii, Ryo*; Nakamura, Masaru*; Imahori, Yoshio*

Interlayer Pd for the Li/Pd/Cu neutron target for BNCT (Boron Neutron Capture Therapy) was characterized after 0.1-5 keV H irradiation by XAFS technique, and following conclusions were derived; (1) From the XAFS observation of white line of Pd, remarkable Pd Edge jump was found in 1.1-3 times higher than before irradiation in low irradiation fluence. (2) This fact indicates increase of hole density in Pd 4d-band, whereas no change was observed for XASF spectra of Ag sample under the same irradiation conditions. (3) Remarkable Pd Edge shift of 0.12-0.66 eV was also found with increase of H irradiation energy in low fluence, and drastically decreased after peak in high irradiation energy and fluence.(4)Implanted protons deposited in Pd as negative under the balance of electron population enhanced by proton irradiation and charge transfer.