Hydrogenation of $$L$$1$$_{2}$$-type AlNi$$_{3}$$ alloy at high pressure and temperature

Endo, Naruki*; Saito, Hiroyuki; Machida, Akihiko; Katayama, Yoshinori

We investigated the hydrogenation of the $$L$$1$$_{2}$$-type AlNi$$_{3}$$ alloy at 3 GPa and 500$$^{circ}$$C using in situ synchrotron radiation X-ray diffraction measurements. An isotropic lattice expansion was observed to have occurred owing to the hydrogenation, and a novel hydride (AlNi$$_{3}$$H$$_{x}$$) was formed. Because of such isotropic lattice expansion, the hydrogen-occupied sites were the body-center sites of the $$L$$1$$_{2}$$ structure (P$$m$$-3$$m$$). In this case, the hydrogen content was calculated to be $$x$$ = 1.0, which is consistent with the experimental results. The AlNi$$_{3}$$H$$_{x}$$ hydride was stable under ambient conditions.



- Accesses




Category:Chemistry, Physical



[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.