Thermal fatigue test on dissimilar welded joint between Gr.91 and 304SS

Wakai, Takashi; Kobayashi, Sumio; Kato, Shoichi; Ando, Masanori; Takasho, Hideki*

This paper describes a thermal fatigue test on a structural model with a dissimilar welded joint. In the present design of JSFR, there may be dissimilar welded joints between ferritic and austenitic steels especially in IHX and SG. Creep-fatigue is one of the most important failure modes in JSFR components. However, the creep-fatigue damage evaluation method has not been established for dissimilar welded joint. To investigate the evaluation method, structural test will be needed for verification. Therefore, a thermal fatigue test on a thick-wall cylinder with a circumferential dissimilar welded joint between Mod.9Cr-1Mo steel and 304SS was performed. Since the coefficients of thermal expansion of these steels were significantly different, buttering layer of Ni base alloy was installed between them. After the completion of the test, deep cracks were observed at the HAZ in 304SS, as well as at HAZ in Mod.9Cr-1Mo steel. There were many tiny surface cracks in BM of 304SS. According to the fatigue damage evaluation based on the finite element analysis results, the largest fatigue damage was calculated at HAZ in 304SS. Large fatigue damage was also estimated at BM of 304SS. Fatigue cracks were observed at HAZ and BM of 304SS in the test, so that analytical results are in a good agreement with the observations. However, though relatively small fatigue damage was estimated at HAZ in Mod.9Cr-1Mo steel, deep fatigue cracks were observed in the test. To identify the cause of such a discrepancy between the test and calculations, we performed a series of finite element analyses. Some metallurgical investigations were also performed.

Accesses

:

- Accesses

InCites™

:

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.