Ion irradiation effects on FeCrAl-ODS ferritic steel

Kondo, Keietsu  ; Aoki, So  ; Yamashita, Shinichiro   ; Ukai, Shigeharu*; Sakamoto, Kan*; Hirai, Mutsumi*; Kimura, Akihiko*

Radiation hardening and microstructural evolution of ion irradiated 12Cr-6Al ODS ferritic steel was studied. Ion irradiation experiments were performed using Fe ions up to the nominal displacement damage of 20 dpa at the irradiation temperature was 300$$^{circ}$$C. The monotonical increase of radiation hardening with dose was confirmed by experimentally obtained hardness data. The radiation hardening was also calculated theoretically by introducing the microstructural character examined by TEM into the dispersed barrier hardening model. The results showed a good agreement with the experimentally obtained data up to 5 dpa, while a slight discrepancy was found between theoretical and experimental hardness values at 20 dpa. Radiation hardening was mainly caused by irradiation-induced defect clusters below the irradiation dose of 5 dpa. As the irradiation dose increased toward 20 dpa, an additional influence of the radiation appeared, which was assumed to be induced by $$alpha$$' phase transformation.

Accesses

:

- Accesses

InCites™

:

Percentile:85.57

Category:Nuclear Science & Technology

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.