Structural investigation of simulated waste glass samples by using XAFS measurement in soft X-ray region (Joint research)

Nagai, Takayuki  ; Okamoto, Yoshihiro  ; Yamagishi, Hirona*; Ota, Toshiaki*; Kojima, Kazuo*; Inose, Takehiko*; Sato, Seiichi*; Hatakeyama, Kiyoshi*

The local structure of glass-forming elements and waste elements in waste glass varies with its chemical composition. In this study, borosilicate glass frit and simulated waste glass samples were prepared and the local structure and chemical state regarding boron (B), oxygen (O), and waste elements of cerium (Ce), cesium (Cs) were estimated by using XAFS measurement in soft X-ray region. Following results were obtained by XAFS measurements of prepared glass frit and simulated waste glass samples: (1) The existence ratio of four coordinate sp structure (BO) tends to increase with increasing NaO content in glass samples. (2) The height of a pre-edge which appears by K-edge XANES spectrum of O is so high that the Fe content in glass samples. Following results were obtained by XAFS measurements of simulated waste glass samples after immersion test to investigate long chemical stability. (1) The existence ratio of four coordinate sp structure (BO) increases by immersion test. (2) Ce which exists in the surface layer is oxidized by immersion test, and much of Cs in surface layer is lost after leach testing. Even if the glass frit form (fiber cartridge or beads) and manufacturing method were changed and a glass sample of the similar chemical composition was prepared, these observed Raman spectra of samples were different.