Nanosecond laser-induced coloration of radiation resistant lead glasses

Yamasaki, Kazuhiko*; Kato, Hironori*; Futakawa, Masatoshi  ; Teshigawara, Makoto   

In this study, coloration and damage of radiation-resistant lead glasses by nanosecond pulse laser with visible wavelength are evaluated. Three kinds of radiation resistance glasses with different lead content: PbO-55 wt%, 71 wt% and PbO free glass are used. As a result, the transitional coloration and damage formation with phase differences had observed by nanosecond pulsed laser irradiation at peak power of 1 kW. Although high-lead concentration glass has lower thresholds for coloration in laser intensity, damage-formation thresholds for both PbO glasses were almost the same. On the other hand, no change was observed after laser-irradiation to PbO-free glass. In addition, photochemical and thermal reaction of PbO by nanosecond pulsed laser irradiation is considered from the result of intensity change at wave numbers 200-500 and 1000 cm in Raman spectrums.