Interaction of solute manganese and nickel atoms with dislocation loops in iron-based alloys irradiated with 2.8 MeV Fe ions at 400 C

Nguyen, B. V. C.*; Murakami, Kenta*; Chena, L.*; Phongsakorn, P. T.*; Chen, X.*; Hashimoto, Takashi; Hwang, T.*; Furusawa, Akinori   ; Suzuki, Tatsuya*

In reactor pressure vessel materials, the formation of Mn- and Ni-rich nanoclusters is a major cause of neutron irradiation embrittlement. The segregation of these solute atoms into dislocation loops has attracted attention as a mechanism to accelerate solute clustering. In this study, the behaviors of solute Mn and Ni atoms in Fe-0.6wt.%Ni, Fe-1.4wt.%Mn, and Fe-1.4wt.%Mn-0.6wt.%Ni alloys irradiated at 400 C up to 3 dpa were analyzed using three-dimensional atom probe tomography. Solute atom clusters were observed in all materials, and their shapes were spherical, flat, and torus in FeNi, FeMn, and FeMnNi, respectively. In ternary alloy FeMnNi, Mn and Ni atoms were concentrated in the sample in the form of arcs, and the orientation of the plane containing the arcs was estimated by comparing field desorption images. The size, number density, and orientation of this structure were found to be in good agreement with those of both types of dislocation loops, namely, b = 1/2 111 and b = 100, identified in a previous study using the same material. The positions of Ni and Mn enrichment did not fully overlap. Ni atoms tended to be concentrated more in the inner part of the loop than the Mn atoms. Mn atoms were enriched only in the vicinity of the dislocation loops, whereas Ni atoms showed a higher concentration inside the dislocation loops than in the bulk.