Laser heating induced spatial homogenization of phase separated Na$$_{2}$$O-B$$_{2}$$O$$_{3}$$-SiO$$_{2}$$ glass plate with bearing NiO for heat center and structural probe

Tomita, Kana*; Kishi, Tetsuo*; Matsumura, Daiju   ; Yano, Tetsuji*

Na$$_{2}$$O-B$$_{2}$$O$$_{3}$$-SiO$$_{2}$$ glass plate phase separated in spinodal was partially remelted and homogenized by laser heating. As heat generation source, 0.8 mol% NiO was added to absorb continuous-wave laser with $$lambda$$=1064 nm. After acid leaching, borate phase with NiO was remaining partially in laser irradiated area. X-ray Absorption Fine Structure (XAFS) spectra revealed that Ni$$^{2+}$$ in laser irradiated area showed coordination change from 6 coordinated octahedral to 5 coordinated in square pyramid along with apparent color change from green to brown. Similar change was observed in water-quenched specimen from 1000$$^{circ}$$C. Ni$$^{2+}$$ transition gave additional structural information in phase separate / homogeneous glass, which was difficult to be distinguished by spectroscopy which focuses on covalent bonding of glass network.

Accesses

:

- Accesses

InCites™

:

Percentile:0.02

Category:Materials Science, Ceramics

Altmetrics

:

[CLARIVATE ANALYTICS], [WEB OF SCIENCE], [HIGHLY CITED PAPER & CUP LOGO] and [HOT PAPER & FIRE LOGO] are trademarks of Clarivate Analytics, and/or its affiliated company or companies, and used herein by permission and/or license.