Tensile properties of modified 316 stainless steel (PNC316) after neutron irradiation over 100 dpa

Yano, Yasuhide  ; Uwaba, Tomoyuki ; Tanno, Takashi  ; Yoshitake, Tsunemitsu ; Otsuka, Satoshi   ; Kaito, Takeji 

The effects of fast neutron irradiation on tensile properties of modified 316 stainless steel (PNC316) claddings and wrappers for fast reactors were investigated. PNC316 claddings and wrappers were irradiated in the experimental fast reactor Joyo at irradiation temperatures between 400 and 735 C to fast neutron doses ranging from 21 to 125 dpa. The post-irradiation tensile tests were carried out at room and irradiation temperatures. Elongations of PNC316 measured by the tensile tests were maintained at an engineering level, although the material incurred significant irradiation hardening and softening. The maximum swelling of PNC316 wrappers was about 2.5 vol.% at irradiation temperature between 400 and 500C up to 110 dpa. Japanese 20% cold-worked austenitic steels, PNC316 and 15Cr-20Ni, had sufficient ductility and work-hardenability even after above 10 vol.% swelling, while they had very weak plastic instabilities.