Effect of grain refinement on transgranular stress corrosion cracking in SUS304L under boiling water reactor conditions

Hirota, Noriaki   ; Nakano, Hiroko  ; Takeda, Ryoma; Ide, Hiroshi  ; Tsuchiya, Kunihiko ; Kobayashi, Yoshinao*

A comparative analysis of the 0.2 % yield stress in SUS304L stainless steel revealed that lower strain rates and higher temperatures significantly reduce yield stress. Grain refinement from 68.6 m to 0.59 m minimally impacted the rate of yield stress reduction at slower strain rates. However, finer grains showed a decrease in yield stress at reactor operating temperature compared to room temperature. In slow strain rate tests under conditions promoting intragranular stress corrosion cracking (SCC), SUS304L with grain sizes of 28.4 m or smaller exhibited similar fracture strains comparable to those at reactor operating temperatures, whereas coarse-grained SUS304L showed reduced fracture strain. Microstructural analysis showed that in smaller grains, over 87 % of the fracture surface was ductile. In particular, SUS304L with 0.59 m grains exhibited a higher presence of {111} / 3 boundaries, which decreased with grain growth. These results indicate that grain refinement will suppress intragranular SCC by slowing corrosion progression through increased {111} / 3 boundaries.