Neutron diffraction study on martensitic transformation under compressive stress in an ordered FePt

福田 隆*; 山口 貴司*; 掛下 知行*; Harjo, S.; 中本 建志*

Journal of Applied Physics, 126(2), p.025107_1 - 025107_6, 2019/07

AA2019-0505.pdf:1.15MB

https://doi.org/10.1063/1.5098960

We have studied the structure change of an ordered FePt (degree of order 0.75) under a compressive stress applied in the [001] direction by neutron diffraction. In the absence of the stress, the alloy exhibits a weak first order martensitic transformation at 90 K from the L1-type cubic structure to the L6-type tetragonal structure. Under the compressive stress of 100 MPa, the first order nature of the thermally-induced martensitic transformation was undetectable in the temperature range of between 70 K and 270 K. The first order nature of the stress-induced martensitic transformation was also undetectable in the stress range of between 6 MPa and 300 MPa when tested at 120 K and higher temperatures. Under these conditions, the lattice parameters change continuously both in the cooling process and in the stress-applying process. A significant stress-induced softening of lattice was observed between 120 K and 265 K but not at 93 K and 295 K.