Oxide particles in oxide dispersion strengthened steel neutron-irradiated up to 158 dpa at Joyo

Toyama, Takeshi*; Tanno, Takashi; Yano, Yasuhide; Inoue, Koji*; Nagai, Yasuyoshi*; Otsuka, Satoshi; Miyazawa, Takeshi; Mitsuhara, Masatoshi*; Nakashima, Hideharu*; Onuma, Masato*; et al.

Journal of Nuclear Materials, 599, p.155252_1 - 155252_14, 2024/10

https://doi.org/10.1016/j.jnucmat.2024.155252

We investigated the stability of oxide nano particles in oxide dispersion-strengthened (ODS) steel, which is a promising candidate material for next-generation reactors, under neutron irradiation at high temperature to high doses. MA957, a 14Cr-ODS steel, was irradiated with Joyo in Japan Atomic Energy Agency under irradiation conditions of 130 dpa at 502C, 154 dpa at 589C, and 158 dpa at 709C. Three-dimensional atom probe (3D-AP) and transmission electron microscope (TEM) observation were performed to characterize the oxide particles in the ODS steels. A high number density of Y-Ti-O particle was observed in the unirradiated and irradiated samples. Almost no change in the morphology of the oxide particles, i.e. average diameter, number density, and chemical composition, has been observed in the samples irradiated to 130 dpa at 502C and to 154 dpa at 589C. A slight decrease in number density was observed in the sample irradiated to 158 dpa at 709CC. The hardness of any of the irradiated samples was almost unchanged from that of the unirradiated sample. It was revealed that the oxide particles existed stable, and the strength of the material was sufficiently maintained even after being neutron irradiated to high dose of 160 dpa at high temperature up to 700C. A part of this study includes the results of MEXT Innovative Nuclear Research and Development Program Grant Number JPMXD0219214482.

Uranium-plutonium-oxygen phase diagram; Investigating the solvus of fluorite's exsolution

Vauchy, R.; Hirooka, Shun; Horii, Yuta; Ogasawara, Masahiro*; Sunaoshi, Takeo*; Yamada, Tadahisa*; Tamura, Tetsuya*; Murakami, Tatsutoshi

Journal of Nuclear Materials, 599, p.155233_1 - 155233_11, 2024/10

https://doi.org/10.1016/j.jnucmat.2024.155233

The fluorite exsolution/recombination in UPuO (y = 0.30 and 0.45) and PuO was investigated using differential scanning calorimetry. The results are in relatively good agreement with the literature data, except for plutonia. Our values indicate that the critical temperature of the miscibility gap in Pu-O is 3050 K lower than previously reported. Finally, the systematic experimental procedure allowed us refining the locus of the solvus existing in hypostoichiometric U0PuO, UPuO, and PuO dioxides.

Interaction of CsOH with structural steel 316L and simulated products of the steel-cladding reaction under assumed conditions relevant for the accident at the Fukushima Dai-Ichi Unit 2 and 3

Pshenichnikov, A.; Zubekhina, B.

Journal of Nuclear Materials, 597, p.155136_1 - 155136_12, 2024/08

https://doi.org/10.1016/j.jnucmat.2024.155136

Formulation of high-temperature strength equation of 9Cr-ODS tempered martensitic steels using the Larson?Miller parameter and life-fraction rule for rupture life assessment in steady-state, transient, and accident conditions of fast reactor fuel

Miyazawa, Takeshi; Tanno, Takashi; Imagawa, Yuya; Hashidate, Ryuta; Yano, Yasuhide; Kaito, Takeji; Otsuka, Satoshi; Mitsuhara, Masatoshi*; Toyama, Takeshi*; Onuma, Masato*; et al.

Journal of Nuclear Materials, 593, p.155008_1 - 155008_16, 2024/05

https://doi.org/10.1016/j.jnucmat.2024.155008

Dissolution behavior and aging of iron-uranium oxide

Tonna, Ryutaro*; Sasaki, Takayuki*; Okamoto, Yoshihiro; Kobayashi, Taishi*; Akiyama, Daisuke*; Kirishima, Akira*; Sato, Nobuaki*

Journal of Nuclear Materials, 589, p.154862_1 - 154862_10, 2024/02

https://doi.org/10.1016/j.jnucmat.2023.154862

The dissolution behavior of FeUO compounds formed by a high-temperature reaction of UO with iron, a stainless-steel component of reactor structural materials, was investigated under atmospheric conditions. The compounds were prepared in an electric furnace using UO and FeO as starting materials, and their solid states were analyzed using X-ray diffraction, scanning electron microscopy energy dispersive X-ray spectroscopy, and X-ray absorption fine structure spectroscopy. The concentration of nuclides dissolved in water was examined by performing static leaching tests of FeUO compounds for up to three months. A redox reaction was proposed to occur between trivalent Fe and pentavalent U ions in the early stage of FeUO dissolution. It was thermodynamically deduced that the reduced divalent Fe ion was finally oxidized into a trivalent ion in the presence of dissolved oxygen, and iron hydroxide limited the solubility of Fe. Meanwhile, the concentration of hexavalent U (i.e., uranyl ion) was limited owing to the presence of secondary minerals such as metaschoepite and sodium uranate and subsequently decreased, possibly owing to sorption on Fe oxides, for example. The concentrations of multivalent ions of fission products, such as Ru and Ce, also decreased, likely for the reason above. By contrast, the concentration of soluble Cs ions did not decrease. The validity of this interpretation was supported by comparing the results with the dissolution behavior of a reference sample (Fe-free UO).

Thermal conductivity measurement of uranium-plutonium mixed oxide doped with Nd/Sm as simulated fission products

Horii, Yuta; Hirooka, Shun; Uno, Hiroki*; Ogasawara, Masahiro*; Tamura, Tetsuya*; Yamada, Tadahisa*; Furusawa, Naoya*; Murakami, Tatsutoshi; Kato, Masato

Journal of Nuclear Materials, 588, p.154799_1 - 154799_20, 2024/01

https://doi.org/10.1016/j.jnucmat.2023.154799

The thermal conductivities of near-stoichiometric (U,Pu,Am)O doped with NdO/SmO, which is major fission product (FP) generated by a uranium-plutonium mixed oxides (MOX) fuel irradiation, as simulated fission products are evaluated at 1073-1673 K. The thermal conductivities are calculated from the thermal diffusivities that are measured using the laser flash method. To evaluate the thermal conductivity from a homogeneity viewpoint of Nd/Sm cations in MOX, the specimens with different homogeneity of Nd/Sm are prepared using two kinds of powder made by ball-mill and fusion methods. A homogeneous Nd/Sm distribution decreases the thermal conductivity of MOX with increasing Nd/Sm content, whereas heterogeneous Nd/Sm has no influence. The effect of Nd/Sm on the thermal conductivity is studied using the classical phonon transport model (A+BT). The dependences of the coefficients A and B on the Nd/Sm content (C and C, respectively) are evaluated as: A(mK/W)=1.70 10 + 0.93C + 1.20C, B(m/W)=2.39 10.

Decontamination and solidification treatment on spent liquid scintillation cocktail

Watanabe, So; Takahatake, Yoko; Ogi, Hiromichi*; Osugi, Takeshi; Taniguchi, Takumi; Sato, Junya; Arai, Tsuyoshi*; Kajinami, Akihiko*

Journal of Nuclear Materials, 585, p.154610_1 - 154610_6, 2023/11

https://doi.org/10.1016/j.jnucmat.2023.154610

Alloy design and characterization of a recrystallized FeCrAl-ODS cladding for accident-tolerant BWR fuels; An Overview of research activity in Japan

Ukai, Shigeharu; Sakamoto, Kan*; Otsuka, Satoshi; Yamashita, Shinichiro; Kimura, Akihiko*

Journal of Nuclear Materials, 583, p.154508_1 - 154508_24, 2023/09

https://doi.org/10.1016/j.jnucmat.2023.154508

Oxygen potential of neodymium-doped UPuAmO uranium-plutonium-americium mixed oxides at 1573, 1773, and 1873 K

Vauchy, R.; Sunaoshi, Takeo*; Hirooka, Shun; Nakamichi, Shinya; Murakami, Tatsutoshi; Kato, Masato

Journal of Nuclear Materials, 580, p.154416_1 - 154416_11, 2023/07

https://doi.org/10.1016/j.jnucmat.2023.154416

Investigation of the oxidation behavior of Zircaloy-4 cladding in a mixture of air and steam

Nemoto, Yoshiyuki; Ishijima, Yasuhiro; Kondo, Keietsu; Fujimura, Yuki; Kaji, Yoshiyuki

Journal of Nuclear Materials, 575, p.154209_1 - 154209_19, 2023/03

https://doi.org/10.1016/j.jnucmat.2022.154209

Previous studies had shown that in certain conditions, the rate of oxidation of zirconium (Zr) based alloy fuel cladding is higher in air-steam mixtures than in dry air. In severe accidents in the spent fuel pool and in other air ingress accidents in nuclear power plants, the cladding is likely to be oxidized in an air-steam mixture, which makes it crucial to have an in-depth understanding of the nature of oxidation and its kinetics in that environment. Oxidation tests were conducted at 800C on Zircaloy-4 specimens in a mix of (air+steam) with various component ratios. Oxidation kinetics, details of the oxide layer, and hydrogen pick-up in the specimen were studied to investigate the mechanism of oxidation in each of these sets of conditions. Zirconium nitride precipitation in the oxide layer during the initial stages of the pre-breakaway oxidation stage and the widespread porous oxide growth on the cladding surface in the latter post-BA oxidation stage are related to the oxidation mechanism in the air-steam mixture. The differences in the mechanism of oxidation of the cladding in dry air and air-steam mixtures are discussed based on the experimental results.