残留オーステナイトを含有する中Mn複合組織鋼の高速変形特性

興津 貴隆*; 北條 智彦*; 諸岡 聡; 宮本 吾郎*

鉄と鋼, 110(3), p.260 - 267, 2024/02

https://doi.org/10.2355/tetsutohagane.TETSU-2023-065

We have investigated the dynamic tensile properties of 4, 5, 6-mass%-Mn-containing low carbon steels with multi-phase microstructures containing retained austenite. The five materials used were classified into two groups. The first group of materials, with around 10% of retained austenite, showed normal strain rete dependence of yield strength (YS) and tensile strength (TS) as in conventional high strength steels. The second group of materials, containing 25-36% of retained austenite, exhibited Lders elongation showed also normal strain rate dependence in YS and flow stress at Lders deformation, but TS varied in a complex manner. Among the second group, in the 4 Mn steel, TS was nearly constant at strain rates below 1 s but increased slightly at higher strain rates. In the 5 and 6 Mn steels, TS once decreased up to the strain rate of 1 or 10 s, and then began to increase at higher strain rates. These behaviors were discussed in terms of temperature rise during plastic deformation causing suppression of martensitic transformation, and thermal stability of retained austenite. In the 4 Mn steel with relatively unstable retained austenite, almost all the austenite transforms regardless of strain rate. In the 5 and 6 Mn steels, where the retained austenite is moderately stable, strain induced transformation of austenite continues up to high plastic strain, providing a good balance of strength and ductility. At high strain rate, TS decreases slightly due to temperature rise, but at higher strain rates than 1 s, the strain rate sensitivity of flow stress in ferrite become prominent and the flow stress increases.