進藤 愛美*; 上奥 あや*; 岡村 和奏*; 菊地 晋; 山崎 淳司*; 古賀 信吉*
Thermochimica Acta, 738, p.179801_1 - 179801_12, 2024/08
被引用回数：1 パーセンタイル：0.00(Thermodynamics)This study investigated the kinetics of the multistep thermal dehydration/decomposition of the metakaolin-based geopolymer paste. The component two reaction steps were characterized by the evolution of water vapor and the simultaneous evolution of water vapor and CO
, respectively. In a stream of dry N, the kinetics of the first and second reaction steps were characterized by the apparent activation energy (Ea) values of 92 and 166 kJ mol
, respectively. Both reaction steps exhibited a diffusion-controlled rate behavior. In a stream of wet N, the mass loss curves systematically shifted to higher temperatures with an increase in the water vapor pressure (p(HO)). The first reaction step was significantly influenced by p(HO), and the apparent Ea increased to 175 kJ mol at p(HO) = 11.4 kPa. The second reaction step was less sensitive to the atmospheric water vapor, as characterized by its Ea of 
165 kJ mol , irrespective of the p(HO).
菊地 晋; 古賀 信吉*; 山崎 淳司*
Journal of Thermal Analysis and Calorimetry, 137(4), p.1211 - 1224, 2019/08
被引用回数：10 パーセンタイル：37.45(Thermodynamics)本研究では、ナトリウム冷却高速炉構造コンクリートに類似した2種類のコンクリートを選定し、これらの熱的挙動の比較検討を実施した。室温から1900Kの温度範囲において、TG-DTAを用いた構造コンクリートの熱的挙動を検討した。コンクリートのセメント部の融解開始温度は1400から1600Kの温度範囲であることが分かった。また、CaCO
とCa(OH)の存在比が異なる2種類のコンクリートのセメント部では、双方の融解温度の範囲に顕著な違いは見られなかった。一方、骨材の融解挙動は当初のシリカの含有量により直接影響を受けることが分かった。
進藤 愛美*; 上奥 あや*; 岡村 和奏*; 菊地 晋; 山崎 淳司*; 古賀 信吉*
no journal, ,
Geopolymer pastes exhibit multistep thermal dehydration/decomposition. Regardless of the samples based on different active fillers including metakaolin (MK), fly ash (FA), and blast furnace slag (BFS), two-step thermal dehydration occurred by partially overlapping, in which the first and second reaction steps were accompanied by the evolutions of water vapor and water vapor with CO, respectively. In this study, the kinetic features of the partially overlapping two-step dehydration processes were investigated at different atmospheric water vapor pressures (p(HO)) to reveal the water vapor release behavior from the geopolymer pastes characterized by a smaller water content.
上奥 あや*; 岡村 和奏*; 近藤 俊樹; 菊地 晋; 山崎 淳司*
no journal, ,
ポルトランドおよびジオポリマーセメントモルタル成形体を一方向から加熱し、成形体表面の水分移動および温度分布変化について、主にハイパースペクトルカメラおよびサーモグラフィーカメラを用いて比較解析した。反射率と温度の関係を明らかにすることで、成形体表面の水分量の増減や内部への移動および脱水が発生する温度や脱水量が明らかになったハイパースペクトルカメラとサーモグラフィカメラの解析結果より、ポルトランドセメントとジオポリマーセメントは異なる加熱挙動を示すことが分かった。
進藤 愛美*; 上奥 あや*; 岡村 和奏*; 菊地 晋; 山崎 淳司*; 古賀 信吉*
no journal, ,
高速炉構造コンクリートの次世代材として、低含水コンクリートの候補の一つであるジオポリマーを検討している。本報告は、メタカオリンをベースとしたジオポリマーペーストを対象にその熱分解挙動を熱分析により追跡した。熱分析の結果から、熱分解による発生ガスの同定を実施するとともに、速度論的分離解析を実施し、脱水挙動の多段階性を評価した。評価の結果、いずれの段階においても拡散律速的挙動であることが分かった。
進藤 愛美*; 上奥 あや*; 岡村 和奏*; 菊地 晋; 山崎 淳司*; 古賀 信吉*
no journal, ,
本研究では、低含水コンクリートの候補材としてフライアッシュをベースとしたジオポリマーペーストと高炉スラグをベースとしたジオポリマーペーストに関する脱水挙動について追跡した。また、それぞれのジオポリマーペーストにおける脱水挙動の性状については、速度論解析の結果から検討し、ジオポリマーペーストの熱分解・脱水挙動は多段階のプロセスで進行することを明らかにした。