Myagmarjav, O.; 柴田 愛*; 田中 伸幸; 野口 弘喜; 久保 真治; 野村 幹弘*; 竹上 弘彰
International Journal of Hydrogen Energy, 46(56), p.28435 - 28449, 2021/08
被引用回数:2 パーセンタイル:8.82(Chemistry, Physical)In this study, a corrosion-stable silica ceramic membrane was developed to be used in H purification during the hydrogen iodide decomposition (2HI H + I), which is a new application of the silica membranes. From a practical perspective, the membrane separation length was enlarged up to 400 mm and one end of the membrane tubes was closed to avoid any thermal variation along the membrane length and sealing issues. The silica membranes consisted of a three-layer structure comprising a porous -AlO ceramic support, an intermediate layer, and a top silica layer. The intermediate layer was composed of -AlO or silica, and the top silica layer that is H selective was prepared via counter-diffusion chemical vapor deposition of a hexyltrimethoxysilane. A membrane using a silica intermediate layer exhibited a higher H/SF selectivity but lower H permeance with compared with the membrane using a -AlO intermediate layer. The membrane using the silica intermediate layer was more stable in corrosive HI gas than a membrane with a -AlO intermediate layer after 300 h of stability tests. To the best of our knowledge, this is the first report of 400-mm-long closed-end silica membranes supported on Si-formed -AlO tubes produced via chemical vapor deposition method. In conclusion, the developed silica membranes seem suitable for membrane reactors that produce H on large scale using HI decomposition in the thermochemical iodine-sulfur process.
三島 理愛; 柴田 裕樹; 佐藤 匠; 林 博和
no journal, ,
マイナーアクチノイド(MA)核変換用窒化物燃料の燃焼により生成する核分裂生成物(FP)元素を含む化合物に関する知見を得るため、単相固溶体型MA窒化物燃料の模擬物質であるGdZrNとPdの高温反応試験を実施した。GdZrNとPd金属を混合成型し、Ar気流中1323Kで加熱して得られた反応後試料について、SEM-EDS測定より、Gd, Zr, Pdからなる反応生成物と、未反応で残存したGdZrNが確認された。XRD測定結果より、試料は未反応のGdZrN,ZrN、及びGdPdと同じ結晶系で格子定数が小さい物質(a=0.40212 0.00004 nm)からなることがわかった。これらの結果から、1323KでのGdZrNとPdの反応によって立方晶系(AuCu型)のGdZrPdが生成することが示された。また、生成したGdZrPd中のGdとZrのモル比はおよそ1:2で、反応前の窒化物固溶体中と比べてZrの比率が小さいことから、本実験条件ではZrよりもGdの方がPdと金属間化合物を生成しやすいことが示唆された。