In situ neutron diffraction during thermo-mechanically controlled process for low alloy steels

友田 陽*; 徐 平光; Oliver, E. C.*; Paradowska, A.*

In-Situ Studies with Photons, Neutrons and Electrons Scattering, p.175 - 190, 2010/12

Neutron diffraction has been employed to study microstructural evolution in situ during heat treatment or thermo-mechanically controlled process for low alloy steels. Transformation kinetics, texture, carbon enrichment and internal stresses can be tracked and these data are useful to develop new processing to realize optimum microstructures.

論文

High-tech composites to ancient metals

Zhang, S. Y.*; Godfrey, E.*; Kockelmann, W.*; Paradowska, A.*; Bull, M. J.*; Korsunsky, A. M.*; Abbey, B.*; 徐 平光; 友田 陽*; Liljedahl, D.*; et al.

Materials Today, 12(7-8), p.78 - 84, 2009/07

 被引用回数:19 パーセンタイル:51.28(Materials Science, Multidisciplinary)

中性子回折は格子面間隔の精密評価に基づいて結晶材料内部の弾性歪みを直接測定できる。無材料除去のままで実際部品の内部組織や変形因子の変化などを非破壊測定的に評価するため、この技術は現代工程材料の設計や古代器物の材料考古学などの分野に特に有効である。本文はISIS核破砕型パルス中性子源に備えたEngin-X中性子回折装置における多数代表性試験研究にめぐって、中性子回折技術は材料科学の深入解明から産業への実際利用まで有効な基礎実験手法であることを示した。

口頭

In situ crystallographic observation of dynamic ferrite transformation evolution during hot deformation of low alloy steels

徐 平光; 友田 陽*; Koo, M.*; 米村 雅雄*; 鈴木 徹也*; Paradowska, A.*; Zhang, S. Y.*; 足立 吉隆*

no journal, , 

動的フェライト変態は鋼組織の超微細化を図る上で重要な手法として注目されている。変態前の母相を加工して格子欠陥密度を増加させ、核生成の優先サイトを増大させると、核生成速度が大きくなり、変態生成物が微細化されることは既に知られている。しかし、加工が変態中に行われる場合、不均一変形が顕著となるためフェライト変態に及ぼす影響が複雑化し、未だ微細化のメカニズムについては不明な点が残されている。本研究は、試料中の特定部位における複数の相の量や内部応力変化を同時にしかも連続的に観察が可能な飛行時間法中性子回折により、低合金鋼の熱間加工中における動的フェライト変態挙動を調査、検討した。

口頭

Dynamic ferrite transformation behavior during hot deformation of low alloy steels studied by neutron diffraction

徐 平光; 友田 陽*; Paradowska, A.*; Vogel, S. C.*

no journal, , 

近年、変形誘発フェライト変態は組織微細化の重要なルートとして重視されてきたが、高加工速度その場実験が困難のため、熱間加工中微細組織の結晶学変化はまだ直接観察されなかった。本研究は飛行時間法中性子回折技術を用いた無加工の静態等温フェライト変態挙動と二つ熱間圧縮速度で熱間加工中の等温変形誘発フェライト変態挙動を比較した。オーステナイト単相域とオーステナイト・フェライト両相域で変形誘発フェライト変態を確認した。

口頭

Ausforming on nano-bainite steel studied by in situ neutron diffraction

Gong, W.; 友田 陽; Harjo, S.; Kelleher, J.*; Paradowska, A.*

no journal, , 

"Nanobainites" with the microstructure consisting of nano-sized lamellar bainitic ferrite and carbon-enriched retained austenite, exhibited a very strong tensile strength of 2 GPa and elongation of 5 %. Although the transformation speed is extremely low in general, we have previously found that it can be accelerated by ausforming. In the present work, in situ TOF neutron diffraction experiment was employed to investigate the kinetic of bainite transformation with and without ausforming, where the bulky averaged microscopic data were evaluated.

口頭

Ausformed bainite transformation behaviors studied by in situ neutron diffraction

Gong, W.; 友田 陽; Harjo, S.; Paradowska, A.*

no journal, , 

In the present work, in situ neutron diffraction during ausformed bainite transformation was carried out with a time-of-flight neutron diffractometer ENGIN-X at the ISIS spallation neutron source, and the non-ausformed bainite transformation was studied by TAKUMI at J-PARC. From the results, it indicates that nanobainite transformation takes place at a narrow temperature regions (473$$sim$$673K). The bainite transformation accelerated by ausforming can be significantly observed in the whole bainite region. The higher carbon diffusion speed in ausforming case should be one reason to accelerate bainite transformation.