Reiser, J. T.*; Neeway, J. J.*; Cooley, S. K.*; Parruzot, B.*; Heredia-Langner, A.*; Gin, S.*; Thomas, M.*; Smith, N. J.*; Icenhower, J. P.*; Stone-Weiss, N.*; et al.
International Journal of Applied Glass Science, 16(4), p.e16707_1 - e16707_16, 2025/10
被引用回数：0 パーセンタイル：0.00(Materials Science, Ceramics)A new technique, termed the stirred-reactor coupon analysis (SRCA) method, has been developed to measure the rate of glass dissolution in forward-rate conditions. Monolithic glass coupons are partially masked with an inert material before placement in a large volume of well-mixed solution with known chemistry and temperature for a predetermined duration. After the test, the mask is removed, and the difference in step height between the protected area and the exposed corroded portions of the sample coupon is measured to determine the extent of glass dissolution. The step height is converted to a rate measurement using the test duration and glass density. Test parameters such as sample surface preparation and test duration were evaluated to determine their effects on the measured rates. Additionally, results from an interlaboratory study (ILS) consisting of 12 laboratories from 11 different institutions are presented, where each laboratory performed 12 independent tests. When removing experimental outlier data, the 95% reproducibility limits for the SRCA method has no statistical difference with previously published standardized test methods used to determine the forward rate of glass dissolution. Overall, this paper describes steps necessary to perform the test method and provides the statistical calculations to evaluate test accuracy.
200 MeV ion irradiationPogrebnjak, A. D.*; Bagdasaryan, A. A.*; Horodeck, P.*; Tarelnyk, V.*; Buranich, V. V.*; 雨倉 宏*; 大久保 成彰; 石川 法人; Beresnev, V. M.*
Materials Letters, 303, p.130548_1 - 130548_4, 2021/11
被引用回数：32 パーセンタイル：84.67(Materials Science, Multidisciplinary)ハイエントロピー合金ベースの(TiZrHfNbV)N窒化物コーティング材に高速重イオン(200MeV Xeイオンビーム)を照射し、陽電子消滅分光法を用いて照射影響を解析した。その結果、照射欠陥のうち、空孔が主な欠陥種であることが分かった。また、5
10
ions/cm
の高照射量まで照射しても非晶質化や金属間化合物の形成は、検知されなかった。ハイエントロピー合金の高い耐照射性を示す結果となった。
Mayoral, M.-L.*; Bobkov, V.*; Colas, L.*; Goniche, M.*; Hosea, J.*; Kwak, J. G.*; Pinsker, R.*; 森山 伸一; Wukitch, S.*; Baity, F. W.*; et al.
Proceedings of 23rd IAEA Fusion Energy Conference (FEC 2010) (CD-ROM), 11 Pages, 2011/03
ITERにおけるイオンサイクロトロン周波数帯(ICRF)加熱装置の最大入射パワーは、アンテナにいかなる設計を採用したとしても、スクレイプオフ層の密度分布に強く依存する。ガス入射によってスクレイプオフ層の密度分布を能動的に制御することで、主プラズマ周辺密度の変化によるICRF波の結合状態の変化を最小化できると考えられている。この手法の特性をさらに詳しく調べるために、国際トカマク物理活動(ITPA)が調整した共同実験が行われた。この実験に参加したすべてのトカマクにおいて、ガス入射を用いたスクレイプオフ層の密度上昇によって結合の改善が得られた。アンテナ前面の密度を上昇させるツールとしてのガス入射の有効性は、広い範囲の実験条件すなわちさまざまなガス入射位置やさまざまなプラズマ形状に対して証明された。また、プラズマ閉じ込めへの有害な影響やアンテナ近傍での有害な相互作用は観測されなかった。