-poly(methyl methacrylate)Zhao, Y.; Sivaniah, E.*; 橋本 竹治
Macromolecules, 41(24), p.9948 - 9951, 2008/12
被引用回数：132 パーセンタイル：96.41(Polymer Science)In this study, the order-disorder transition (ODT) for two symmetric polystyrene-b-poly(methyl methacrylate) diblock copolymers was investigated by a high temperature-resolution Small Angle X-ray Scattering (SAXS) experiments with small decreases of temperature (T) across the ODT. The characteristic ODT temperature was determined from the discontinuity of 1/Im and q2 vs 1/T, confirming the fluctuation-induced weakly first-order transition for this block copolymer. In the disordered state, far above ODT temperature, the interaction parameter for PS-b-PMMA was also extracted, and found to be slightly larger than that in the deuterated systems having the similar molecular weight and compositions. PS-b-PMMA is a promising technological system that is able to be manipulated to provide nanostructural templates and scaffolds. Hence our precise determination of the interaction parameter and the order-disorder characteristics of a non-deuterated system will be invaluable to future works.
Sivaniah, E.*; 松原 真也*; Zhao, Y.; 橋本 竹治; 福永 謙二*; Kramer, E. J.*; Mates, T. E.*
Macromolecules, 41(7), p.2584 - 2592, 2008/04
被引用回数：36 パーセンタイル：71.86(Polymer Science)The lamellar dimension, D, for pure and blended block copolymer (BCPs) thin films of symmetricpoly(styrene)-block-poly(methyl methacrylate) was measured using atomic force microscopy analysis of surface patterns of perpendicularly oriented lamellar structures. It was approximately verified, using SAXS and AFM analysis, that perpendicular structures in lamellar thin films bounded by a neutral and a roughened interface did not significantly alter the bulk block copolymer phase separation thermodynamics. In the case of blends, it was also verified that there was a uniform distribution of blend components throughout the thin film.
安達 雅幸*; 奥村 有道*; Sivaniah, E.*; 橋本 竹治
Macromolecules, 39(21), p.7352 - 7357, 2006/10
被引用回数：35 パーセンタイル：69.63(Polymer Science)この研究では、まず二元ブロック共重合体バルクが形成する秩序の高いミクロ相分離構造の一つの相を空孔にした新奇なナノ構造を有する鋳型を形成した。ついで、この鋳型にパラジウムナノ微粒子を導入することを目的とした。このためにまずポリイソプレン-ポリビニルピリジン二元ブロック共重合体を試料として用いて、ポリイソプレン相がマトリックス相でポリビニルピリジン相がネットワークを形成する共連続二重ジャイロイド秩序構造を構築した。次いでマトリックス相をオゾン分解処理して、空孔の体積分率が64%の高空孔率を有し、かつ高比表面積を有する二重ジャイロイドネットワーク構造を構築した。これをパラジウムイオンを含むベンゼン/プロパノール混合溶液中に含浸し、パラジウムイオンを還元することにより、二重ジャイロイドネットワーク構造中にパラジウムナノ微粒子を形成させた。ナノ微粒子の成長機構を解明するとともに、ナノ微粒子の数密度,粒子直径(5から10ナノメートル)を制御することに成功した。