山中 謙太*; 黒田 あす美*; 伊藤 美優*; 森 真奈美*; Bian, H.*; 菖蒲 敬久; 佐藤 茂男*; 千葉 明彦*
Additive Manufacturing, 37, p.101678_1 - 101678_12, 2021/01
被引用回数：23 パーセンタイル：86.72(Engineering, Manufacturing)Ti-6Al-4V alloy is widely used in aerospace and biomedical industries, and its preparation using additive manufacturing techniques has recently attracted considerable attention. Herein, the dislocation structures developed during electron beam and laser beam powder-bed fusion (EB-PBF and LB-PBF, respectively) of the Ti-6Al-4V alloy were quantitatively examined via XRD line profile analysis. Accordingly, a higher dislocation density and finer crystallite size were observed at the top cross-section from the XRD line profile analysis, suggesting that the extent of phase decomposition depended on the duration of the exposure to the elevated temperature. Nonetheless, the saturated dislocation density was as high as 10
m
, where dislocation strengthening affected the overall strength of the EB-PBF specimen. Diffraction peaks of sufficient intensity that enabled the analysis of the dislocation structures in both the 
(')-matrix and the nanosized beta-phase precipitates at the (')-laths were obtained under high-energy synchrotron radiation; this revealed that the beta-phase had a much higher dislocation density than the surrounding (')-matrix. The enhanced dislocation accumulation in the nanosized 
-phase precipitates probably reflects the elemental partitioning that occurred during post-solidification cooling. The valuable insights provided in this study are expected to promote further development of alloy preparation using additive manufacturing processes.
-to-
martensitic transformation of biomedical Co-Cr-Mo alloys by introducing parent phase lattice defects森 真奈美*; 山中 謙太*; 佐藤 茂男*; 椿 真貴*; 佐藤 こずえ*; 熊谷 正芳*; 今福 宗行*; 菖蒲 敬久; 千葉 明彦*
Journal of the Mechanical Behavior of Biomedical Materials, 90, p.523 - 529, 2019/02
被引用回数：19 パーセンタイル：71.16(Engineering, Biomedical)In this study, we examined the effect of pre-existing dislocation structures in a face-centered cubic gamma-phase on strain-induced martensitic transformation (SIMT) to produce a hexagonal close-packed epsilon-phase in a hot-rolled biomedical Co-Cr-Mo alloy. The as-rolled microstructure was characterized by numerous dislocations as well as stacking faults and deformation twins. SIMT occurred just after macroscopic yielding in tensile deformation. Using synchrotron X-ray diffraction line-profile analysis, we successfully captured the nucleation of epsilon-martensite during tensile deformation in terms of structural evolution in the surrounding gamma-matrix: many dislocations that were introduced into the gamma-matrix during the hot-rolling process were consumed to produce epsilon-martensite, together with strong interactions between dislocations in the gamma-matrix. As a result, the SIMT behavior during tensile deformation was accelerated through the consumption of these lattice defects, and the nucleation sites for the SIMT epsilon-phase transformed into intergranular regions upon hot rolling. Consequently, the hot-rolled Co-Cr-Mo alloy simultaneously exhibited an enhanced strain hardening and a high yield strength. The results of this study suggest the possibility of a novel approach for controlling the to SIMT behavior, and ultimately, the performance of the alloy in service by manipulating the initial dislocation structures.
山本 正弘; 加藤 千明; 佐藤 智徳; 中野 純一; 宇賀地 弘和; 塚田 隆; 加治 芳行; 辻川 茂男*; 服部 成雄*; 吉井 紹泰*; et al.
JAEA-Review 2012-007, 404 Pages, 2012/03
JAEA-Review-2012-007.pdf:36.72MB
我が国の軽水炉は運転開始から20年以上経過したものが多くを占め、経年劣化に対応した技術を確立して安全に運転していくことが望まれている。特にSCCについては、これまでに幾つかのトラブル事象が報告されており、対応技術やメカニズムに関する数多くの研究例がある。今回、それらをできるだけ広く集めて整理し、体系的にレビューした。具体的には、軽水炉に発生したSCC事例とその評価の現状、SCC発生・進展因子に関する評価法の研究と知見の現状、SCC・腐食環境のモニタリング技術の現状等について調査を行った。調査した結果は、炉型(BWR, PWR),材料(ステンレス鋼,Ni基合金)及びSCC評価法(ラボと実機)について、横断的かつ総合的に検討を行い、それらの共通点,相違点を理解しやすい図表として整理し、相対的な比較を行いやすいようにまとめた。これらの整理した結果を元に、今後検討すべき課題を抽出し、また実機において留意していくべき事象に関してまとめた。ラボ試験における加速条件の評価においては、最新の解析技術を駆使したミクロな解析と統計的な手法を含めた計算機的な予測やモデル化技術が今後重要になることを示した。また、実機の状況を運転中に把握し、SCCが顕在化する以前の兆候をモニタリングする手法の重要性を示し、今後実用化を含めた検討が必要であることを示した。
都筑 和泰; 木村 晴行; 川島 寿人; 佐藤 正泰; 神谷 健作; 篠原 孝司; 小川 宏明; 星野 克道; Bakhtiari, M.; 河西 敏; et al.
Nuclear Fusion, 43(10), p.1288 - 1293, 2003/10
被引用回数：39 パーセンタイル：74.23(Physics, Fluids & Plasmas)JFT-2Mでは、原型炉のブランケット構造材料の候補である低放射化フェライト鋼とプラズマとの適合性を調べる実験を進めてきている。昨年度にはフェライト鋼内壁を真空容器内に全面的に設置する作業を行い、今年度より実験を開始している。プラズマ生成,制御は問題なく行われ、金属不純物の放出も検出限界以下であった。改善閉じ込め(Hモード)も実現され、そのしきいパワーもこれまでと同等であった。プラズマ安定性に関してもこれまでの所悪影響は観測されておらず、規格化が3を超える放電との共存性も示された。高速イオンのリップル損失に関しても顕著な低減が実証された。以上のように、フェライト鋼の悪影響は小さく、有望な結果を得ている。JFT-2Mでは、その他にも先進的、基礎的な研究を行っている。先進的粒子供給手法であるコンパクトトロイド(CT)入射実験においては、再現性よくプラズマ中へ入射が行われ、CT入射に伴う密度の急上昇が初めて明確に観測された。
佐藤 智徳; 山本 正弘; 大森 千広*; 野村 昌弘; 辻川 茂男*; 小川 洋之*; 中島 博志*
no journal, ,
大強度陽子加速器施設J-PARCの鉄ベースの金属磁性体を用いた高周波加速空洞は、電流を流すことで加熱するために、循環水で冷却されている。この金属磁性体の金属面が腐食しているような形態が観察され、粒子加速性能の低下が確認された。そこで、この腐食現象の解明と対策を考えることを目的として、腐食解析を実施した。その結果、水中の銅イオンの寄与が明らかとなった。また、銅イオンフリー条件で腐食速度は40
m/年であり、腐食対策が必要であることが明らかとなった。