鈴木 賢治*; 菖蒲 敬久; 和田 国彦*; 松原 秀彰*; 川村 昌志*
材料, 57(7), p.674 - 680, 2008/07
CoNiCrAlY was pressureless plasma-sprayed on a substrate of nickel-base superalloy as a bond coating. Under the substrate rotation, zirconia with 4mol yttria was coated as the top coating by the electron beam-physical vapor deposition (EB-PVD). The rotation speed of the substrate was 5, 10 and 20rpm. The top coating was made by the columnar structure which consisted of the core part and the peripheral part. The top of the core part had a pyramidal shape made by piling up the zirconia (111) planes. The peripheral part showed feather-like structure, which was made by growth of the zirconia 
100
and (111) directions. By the increase in the rotation speed, the column becomes thick and the inter-columnar space becomes large. The substrate rotation is useful for the reduction of the residual stresses in the EB-PVD thermal barrier coating.
鈴木 賢治*; 菖蒲 敬久; 和田 国彦*; 松原 秀彰*
日本機械学会論文集,A, 74(739), p.370 - 376, 2008/03
ガスタービンエンジンの主要技術である遮熱コーティングに関して、高温大気曝露を施した試験片における残留応力及び組織観察を行い、曝露前との比較することによる材料挙動を検討した。高エネルギー放射光X線による非破壊応力測定の結果、コーティング表面から中間層において圧縮応力が開放されつつあり、組織観察からその原因は焼結による羽毛状組織の凝集が影響していると考えられる。また、ボンドコーティングとの界面付近のトップコーティング初期層では残留応力が解放されずに圧縮の面内残留応力が残っており、これはボンドコーティングと基材との熱膨張係数のミスマッチが影響していると考えられる。
鈴木 賢治*; 和田 国彦*; 松原 秀彰*; 菖蒲 敬久; 川村 昌志*; 田中 啓介*
材料, 56(7), p.588 - 593, 2007/07
Niベースの超合金であるIN738LCは基質材料として使われ、CoNiCrAlYはその上にボンドコートとしてプラズマスプレーにより押し固められている。その上にZrがEV-PVD法によりトップコーティングされている。本試験では基盤回転数の異なる試料に関して、組織観察及び残留応力測定を行った。SEM観察の結果から、Zrコーティングは(111)方向に成長した柱状組織を有していることがわかった。また表面の残留応力は、基盤回転数が減少するに従い圧縮の残留応力が大きくなることがわかった。