石井 悠衣*; 山本 有梨沙*; 佐藤 直大*; 南部 雄亮*; 河村 聖子; 村井 直樹; 尾原 幸治*; 河口 彰吾*; 森 孝雄*; 森 茂生*
Physical Review B, 106(13), p.134111_1 - 134111_7, 2022/10
被引用回数：0 パーセンタイル：0(Materials Science, Multidisciplinary)We report that complete suppression of a phonon-driven structural phase transition causes partial breakdown of a three-dimensional translation symmetry in a well-defined sublattice. This state is revealed for a dielectric compound, Ba
Sr
Al
O
, that comprises an AlO network incorporated into a hexagonal Ba(Sr) sublattice. Pair distribution function analyses and inelastic neutron scattering experiments provide clear-cut evidence of the AlO network forming a continuum of Al-O short-range correlations similar to glasses, whereas the Ba(Sr) sublattice preserves the original translational symmetry. This glassy network significantly dampens the phonon spectrum and transforms it into the broad one resembling those typically observed in glass materials.
Sb
O
F observed by high-resolution synchrotron and neutron diffraction下野 聖矢*; 石橋 広記*; 永吉 祐輔*; 池野 豪一*; 河口 彰吾*; 萩原 雅人; 鳥居 周輝*; 神山 崇*; 市橋 克哉*; 西原 禎文*; et al.
Journal of Physics and Chemistry of Solids, 163, p.110568_1 - 110568_7, 2022/04
被引用回数：1 パーセンタイル：15.7(Chemistry, Multidisciplinary)The structural phase transition from cubic (
) to a 
tetragonal (
) at 
180 K was found in non-centrosymmetric oxyfluoride CoSbOF by high-resolution neutron and synchrotron powder diffraction. To investigate this phase transition, specific heat, magnetization, and dielectric measurements were performed. Although the specific heat and dielectric constant showed anomalies at , a phase transition to ferroelectricity was not observed in the polarization hysteresis loop down to 30 K. The rotation of the CoO
F octahedron was observed at from the structural analysis using synchrotron and neutron powder diffraction data. It was found that the magnetic phase transition from paramagnetic to G-type antiferromagnetic occurred at 
67 K, at which a peak was observed in the specific heat measurements, via magnetic structure analysis using neutron powder diffraction data. The magnetic moments of Co
were aligned along the tetragonal 
-axis direction with a Co moment of 2.80(1) 
at 13 K.
Li, B.*; 川北 至信; 河村 聖子; 菅原 武*; Wang, H.*; Wang, J.*; Chen, Y.*; 河口 沙織*; 河口 彰吾*; 尾原 幸治*; et al.
Nature, 567(7749), p.506 - 510, 2019/03
被引用回数：182 パーセンタイル：99.31(Multidisciplinary Sciences)冷却は現代社会では、世界における25-30%の電力が空調や食料保存に用いられるように、重要である。従来の気化、圧縮で冷却を行う方法は、温暖化などの観点から限界が来ている。有望な代替手段として固体の熱量効果を用いた冷却方法が注目を集めている。しかしながら、この方法は、現在候補に挙げられている物質ではエントロピー変化の小ささや巨大な磁場を必要とするところなどから性能に限界がある。そこで我々は柔粘性結晶における圧力誘起の相転移で冷却が起こる巨大圧力熱量効果を報告する。柔粘性結晶の一つであるネオペンチルグリコールのエントロピー変化は室温近傍において単位キログラム、単位温度あたり、約389ジュールであった。圧力下の中性子散乱実験の結果から、そのような巨大圧力熱量効果は分子配向の非秩序化、巨大な圧縮率、極めて非線形性の強い格子ダイナミクスの組み合わせに由来することが明らかになった。我々の研究により、柔粘性結晶における巨大圧力熱量効果発現の微視的機構が明らかとなり、次世代の固体を使った冷却技術の確立に筋道を付けることができた。