鈴木 徹也*; 山中 啓輔*; 石野 まゆ子*; 篠原 康浩*; 長井 健介*; 津留 英司*; 徐 平光
鉄と鋼, 98(6), p.262 - 266, 2012/06
The work-hardening characteristics of anisotropic tensile deformations and the corresponding residual strain changes of pre-strained ferritic steels without and with ageing treatment were investigated by using angle dispersive neutron diffraction and electron back-scattering diffraction. The plastic deformation along the pre-strained direction leads to evident work-hardening at the beginning stage, showing discontinuous yielding behavior. Comparably, the plastic deformation perpendicular to the pre-strained direction shows continuously yielding. The tensile and compressive residual strains were found in the 200 and 110 grains along the pre-strained direction, respectively. It is also found that the difference in various oriented grains after strain ageing become more evident along the pre-strained direction but smaller perpendicular to the pre-strained direction, revealing a higher work hardening capability in the former case than in the latter case.
鈴木 徹也*; 山中 啓輔*; 長井 健介*; 津留 英司*; 徐 平光; 鈴木 裕士
no journal, ,
ひずみ時効硬化は予ひずみを与えた後に時効処理を施すことで生じる。多結晶材料は負荷方向に対する変形の容易性が結晶粒ごとに異なるため、予ひずみ導入時に各結晶に発生する転位の量には結晶方位により分布があると推測される。このことにより、時効処理によって硬化する粒にも結晶方位による分布が存在すると考えられる。本研究ではフェライト単相鋼を用いて予ひずみ導入後に変形方向を変えて引張試験を行った。時効処理前後における残留応力を中性子回折により測定し、ひずみ時効硬化の方位依存性について検討した。初期材のピーク位置と比較して予ひずみ材のピーク位置が変化している。このことから予ひずみの導入により、結晶粒ごとの強度の異方性から残留ひずみが生じていることがわかった。