小山 元道*; 山下 享介*; 諸岡 聡; 澤口 孝宏*; Yang, Z.*; 北條 智彦*; 川崎 卓郎; Harjo, S.
鉄と鋼, 110(3), p.197 - 204, 2024/02
The local plasticity and associated microstructure evolution in Fe-5Mn-0.1C medium-Mn steel (wt.%) were investigated in this study. Specifically, the micro-deformation mechanism during L
ders banding was characterized based on multi-scale electron backscatter diffraction measurements and electron channeling contrast imaging. Similar to other medium-Mn steels, the Fe-5Mn-0.1C steel showed discontinuous macroscopic deformation, preferential plastic deformation in austenite, and deformation-induced martensitic transformation during Lders deformation. Hexagonal close-packed martensite was also observed as an intermediate phase. Furthermore, an in-situ neutron diffraction experiment revealed that the pre-existing body- centered cubic phase, which was mainly ferrite, was a minor deformation path, although ferrite was the major constituent phase.
neutron diffraction澤口 孝宏*; 友田 陽*; 吉中 奎貴*; Harjo, S.
Acta Materialia, 242, p.118494_1 - 118494_14, 2023/01
被引用回数：4 パーセンタイル：45.58(Materials Science, Multidisciplinary)Fe-Mn-Si-based alloys, show superior resistance to plastic fatigue compared to the conventional steels, which is ascribed to the reversible back-and-forth movement of Shockley partial dislocations associated with a reversible martensitic transformation between the face-centered cubic 
-austenite and hexagonal close-packed 
-martensite. The purpose of this study was to gather evidence of the reversible martensitic transformation using in situ neutron diffraction under cyclic loading. Three Fe-30Mn-Si-Al alloys with different Gibbs free energy differences at 298 K were studied to unravel the effect of phase stability on the degree of reversibility.
ders deformation in an Fe-5Mn-0.1C medium-Mn steel小山 元道*; 山下 享介*; 諸岡 聡; 澤口 孝宏*; Yang, Z.*; 北條 智彦*; 川崎 卓郎; Harjo, S.
ISIJ International, 62(10), p.2036 - 2042, 2022/10
被引用回数：5 パーセンタイル：64.46(Metallurgy & Metallurgical Engineering)The local plasticity and associated microstructure evolution in Fe-5Mn-0.1C medium-Mn steel (wt.%) were investigated in this study. Specifically, the micro-deformation mechanism during Lders banding was characterized based on multi-scale electron backscatter diffraction measurements and electron channeling contrast imaging. Similar to other medium-Mn steels, the Fe-5Mn-0.1C steel showed discontinuous macroscopic deformation, preferential plastic deformation in austenite, and deformation-induced martensitic transformation during Lders deformation. Hexagonal close-packed martensite was also observed as an intermediate phase. Furthermore, an in-situ neutron diffraction experiment revealed that the pre-existing body-centered cubic phase, which was mainly ferrite, was a minor deformation path, although ferrite was the major constituent phase.
小山 元道*; 北條 智彦*; 宮本 吾郎*; 諸岡 聡; 山下 享介; 澤口 孝宏*; 峯 洋二*; 眞山 剛*; 興津 貴隆*; 榊原 睦海*; et al.
no journal, ,
高強度-高延性鋼を開発するために近年盛んに研究されてきた対象は、高Mn鋼と変態誘起塑性(TRIP)鋼である。高Mn鋼の研究を通して、Mn利用による積層欠陥エネルギーおよび相変態挙動の制御の重要性が再認識された。また、素材コストも睨みながら、従来の延性強度バランスを打破するには、未変態オーステナイトのTRIP効果を利用することが有効であるとの見方も広く受け入れられてきた。これら高Mn鋼とTRIP鋼の研究が合流する形で、TRIP効果を示す中Mn鋼が注目されている。中Mn鋼は優れた延性強度バランスを示す。しかし、複相であること、化学組成や熱処理条件に敏感であること、変形誘起マルテンサイト変態を示すこと、大きなリューダース変形を示すこと、応力ひずみ応答においてセレーションが現れること等に起因して、非常に複雑な塑性変形挙動を呈する。そのため、その優れた力学特性発現の機構は未だ不明瞭である。本講演では、その優れた力学特性の原因を組織発達および塑性変形挙動解析に基づいて明らかとするための研究戦略を示し、その妥当性と応用展開を広く議論する。
諸岡 聡; 川崎 卓郎; Harjo, S.; 山下 享介*; 小山 元道*; 澤口 孝宏*; 芳賀 芳範
no journal, ,
第3世代先進高張力鋼とされるQ&P鋼や5mass%前後のMnを添加した中Mn鋼等は、フェライト,マルテンサイト、及びオーステナイトを利用している。この三相の微視組織では、オーステナイトの存在により、鋼は塑性変形をさらに拡大することができ、オーステナイト自体が塑性変形すると、マルテンサイトに変態し、鋼の全体的な強度が向上する。特に、Millerにより提起された中Mn鋼は、2相域焼鈍し、その温度に保持することで、高温域におけるオーステナイト中にC, Mnを濃化させ、30vol.%以上の多量のオーステナイトを残存させることを可能とした。その結果として、第3世代先進高張力鋼の目標に合致する優れた強度-延性バランスを発揮することができる。これまで、Koyamaらは、5Mn-0.1C鋼において、室温における機械特性と詳細な微視組織観察の結果から変形機構の解明を進めている。一方で、Yamashitaらは、低温における機械特性を評価し、室温(298K)と比較して、降伏強度が非常に高くなることを報告しているが、その原因については言及していない。そこで、本研究では、中性子回折法による低温環境下その場測定を用いて、5Mn-0.1C鋼の低温挙動を観測し、低温環境における特異な力学特性の解明を進めることを目的とする。