Liu, Y.*; 宮田 登*; 宮崎 司*; 春藤 淳臣*; 川口 大輔*; 田中 敬二*; 青木 裕之
Langmuir, 39(29), p.10154 - 10162, 2023/06
被引用回数：1 パーセンタイル：52.07(Chemistry, Multidisciplinary)Water absorbed by epoxy resins from a humid atmosphere considerably influences their structure and properties. Examining the effects of absorbed water on epoxy resins at their interfaces with solid substrates is crucial because of their adhesive applications in various fields. The spatial distribution of absorbed water in epoxy resin thin films under high humidity was investigated in this study by neutron reflectometry. Water molecules were found to accumulate at the SiO
/epoxy resin interface after exposure at a relative humidity of 85% for 8 h. The formation of an ca.1 nm-thick condensed water layer was observed, and the thickness of this layer varied with curing conditions of epoxy systems. Furthermore, the water accumulation at the interface was noted to be affected by high-temperature and high-humidity environments. The formation of the condensed water layer is presumed to be related to the features of the polymer layer near the interface. The construction of the interface layer of epoxy resin would be affected by the interface constraint effect on the cross-linked polymer chain during the curing reaction. This study provides essential information for understanding the factors influencing the accumulation of water at the interface in epoxy resins. In the practical application, the process of improving the construction of epoxy resin near the interface would be a reasonable solution to resist the water accumulation in the interface.
Yamaguchi, Ko*; 川口 大輔*; 宮田 登*; 宮崎 司*; 青木 裕之; Yamamoto, Satoru*; 田中 敬二*
Physical Chemistry Chemical Physics, 24(36), p.21578 - 21582, 2022/09
被引用回数：5 パーセンタイル：70.33(Chemistry, Physical)A better understanding of the chemical reaction between epoxy and amine compounds at a solid interface is crucial for the design and fabrication of materials with appropriate adhesive strength. Here, we examined the curing reaction kinetics of epoxy phenol novolac and 4,4'-diaminodiphenyl sulfone at the outermost interface using sum-frequency generation spectroscopy, and X-ray and neutron reflectivity in conjunction with a full atomistic molecular dynamics simulation. The reaction rate constant was much larger at the quartz interface than in the bulk. While the apparent activation energy at the quartz interface obtained from an Arrhenius plot was almost identical to the bulk value, the frequency factor at the quartz interface was greater than that in the bulk. These results could be explained in terms of the densification and orientation of reactants at the interface, facilitating the encounter of the reactants present.
宮崎 司*; 宮田 登*; 吉田 鉄生*; 有馬 寛*; 津村 佳弘*; 鳥飼 直也*; 青木 裕之; 山本 勝宏*; 金谷 利治*; 川口 大輔*; et al.
Langmuir, 36(13), p.3415 - 3424, 2020/04
被引用回数：14 パーセンタイル：58.64(Chemistry, Multidisciplinary)We investigated in detail the structures in the poly(vinyl alcohol) (PVA) adsorption layers on a Si substrate, which remained on the substrate after immersing the relatively thick 30 - 50 nm films in hot water, by neutron reflectometry under humid conditions. For the PVA with a degree of saponification exceeding 98 mol %, the adsorption layer exhibits a three-layered structure in the thickness direction. The bottom layer is considered to be the so-called inner adsorption layer that is not fully swollen with water vapor. This may be because the polymer chains in the inner adsorption layer are strongly constrained onto the substrate, which inhibits water vapor penetration. The polymer chains in this layer have many contact points to the substrate via the hydrogen bonding between the hydroxyl groups in the polymer chain and the silanol groups on the surface of the Si substrate and consequently exhibit extremely slow dynamics. Therefore, it is inferred that the bottom layer is fully amorphous. Furthermore, we consider the middle layer to be somewhat amorphous because parts of the molecular chains are pinned below the interface between the middle and bottom layers. The molecular chains in the top layer become more mobile and ordered, owing to the large distance from the strongly constrained bottom layer; therefore, they exhibit a much lower degree of swelling compared to the middle amorphous layer. Meanwhile, for the PVA with a much lower degree of saponification, the adsorption layer structure consists of the two-layers. The bottom layer forms the inner adsorption layer that moderately swells with water vapor because the polymer chains have few contact points to the substrate. The molecular chains in the middle layer, therefore, are somewhat crystallizable because of this weak constraint.
宮崎 司*; 宮田 登*; 浅田 光則*; 津村 佳弘*; 鳥飼 直也*; 青木 裕之; 山本 勝宏*; 金谷 利治*; 川口 大輔*; 田中 敬二*
Langmuir, 35(34), p.11099 - 11107, 2019/08
被引用回数：22 パーセンタイル：67.64(Chemistry, Multidisciplinary)We investigated the swelling behaviors of poly(vinyl alcohol) (PVA) films deposited on Si wafers with water vapor, which is a good solvent for PVA for elucidating structural and dynamical heterogeneities in the film thickness direction. Using deuterated water vapor, structural and dynamical differences in the thickness direction can be detected easily as different degrees of swelling in the thickness direction by neutron reflectivity. Consequently, the PVA film with a degree of saponification exceeding 98 mol % exhibits a three-layered structure in the thickness direction. It is considered that an adsorption layer consisting of molecular chains that are strongly adsorbed onto the solid substrate is formed at the interface with the substrate, which is not swollen with water vapor compared with the bulk-like layer above it. The adsorption layer is considered to exhibit significantly slower dynamics than the bulk. Furthermore, a surface layer that swells excessively compared with the underneath bulk-like layer is found. This excess swelling of the surface layer may be related to a higher mobility of the molecular chains or lower crystallinity at the surface region compared to the underneath bulk-like layer. Meanwhile, for the PVA film with a much lower degree of saponification, a thin layer with a slightly lower degree of swelling than the bulk-like layer above it can be detected at the interface between the film and substrate only under a high humidity condition. This layer is considered to be the adsorption layer composed of molecular chains loosely adsorbed onto the Si substrate.