金井 亮彦*; Park, C.*; 登尾 一幸*; 笠田 竜太*; 小西 哲之*; 廣瀬 貴規; 野澤 貴史; 谷川 博康
Fusion Engineering and Design, 89(7-8), p.1653 - 1657, 2014/10
被引用回数:4 パーセンタイル:31.13(Nuclear Science & Technology)The present study reports the compatibility of a reduced-activation ferritic steel F82H and Ni exposed to liquid Pb-Li flow using a rotating disk apparatus at 873 K. Cross-sectional observations revealed that grain boundary attack of Pb caused a liquid metal embrittlement of Ni and formation of pitting holes and Cr-depleted zone in F82H.