矢田 浩基; 金川 晃大*; 服部 修次*
日本機械学会論文集,B, 78(788), p.811 - 820, 2012/04
液体金属噴流によるキャビテーション試験が可能な試験ループを開発し、融点が68
Cの低融点合金(PbBi-68)を用いた液体金属流れ系でキャビテーション初生試験及び壊食試験を行った。加速度センサを用いて検出した初生キャビテーション数は水中及びPbBi-68中でほぼ等しく、流速依存性は見られない。また、異なる形状のノズルを用いて水中で試験を行い、初生キャビテーション数は下流圧と実測の流速から求めたキャビテーション数を用いて評価することによりノズル形状にかかわらずほぼ同じ値となること、各ノズルでの壊食速度は加速度センサ出力電圧の大小関係と定性的に一致することが明らかとなった。
金川 晃大*; 矢田 浩基; 月森 和之; 服部 修次*
no journal, ,
The cavitation erosion in liquid metal is important for the safety of the nuclear reactor and the industrial equipment. However, a study on the cavitation erosion in liquid metal has not been developed. This study clarified the incipient condition of cavitation in tap water and liquid metal. A test apparatus for Pb-Bi alloy was developed. It was found that the incipient cavitation number in tap water is about 0.8. The incipient cavitation number in Pb-Bi alloy is 0.8. The incipient cavitation number is the same value regardless of kinds of test liquid. And this study clarified an incipient condition of cavitation with different shape of orifice. When the cavitation number was defined by using flow velocity, the incipient cavitation number becomes constant level regardless of the orifice shape. A test apparatus for the erosion tests was developed.
服部 修次*; 金川 晃大*; 矢田 浩基
no journal, ,
The cavitation erosion in liquid metal is important for the safety of the nuclear reactor and the industrial equipment. However, a study on the cavitation erosion in liquid metal has not been developed. This study clarified the incipient condition of cavitation in tap water and liquid metal. A test apparatus for Pb-Bi alloy was developed. It was found that the incipient cavitation number in tap water is about 0.8. The incipient cavitation number in Pb-Bi alloy is 0.8. The incipient cavitation number is the same value regardless of kinds of test liquid. This study also clarified an incipient condition of cavitation with different shape of orifice. When the cavitation number was defined by using flow velocity, the incipient cavitation number becomes constant regardless of the orifice shape. A test apparatus for the erosion tests was developed.
矢田 浩基; 金川 晃大*; 服部 修次*
no journal, ,
流体機械におけるキャビテーションの発生は、機器の性能低下や損傷を引き起こすことが知られている。磁わい振動試験による壊食試験では、壊食速度は水中に比べ、鉛ビスマス中では約10倍、ナトリウム中では約2
5倍となる。キャビテーションの発生を防止,抑制するには、キャビテーションの発生条件を知ることが重要であることから、本研究では、低融点合金を用いた試験が可能なキャビテーション噴流試験装置を開発し、水中及び鉛ビスマス低融点合金を用いてキャビテーション初生試験について検討した。また、噴流試験に用いるノズル形状がキャビテーション初生条件に及ぼす影響について検討するため、数種類のノズルを用いた試験を行った。