Improving fatigue performance of laser-welded 2024-T3 aluminum alloy using dry laser peening

Sano, Tomokazu*; Eimura, Takayuki*; Hirose, Akio*; Kawahito, Yosuke*; Katayama, Seiji*; Arakawa, Kazuto*; Masaki, Kiyotaka*; Shiro, Ayumi*; Shobu, Takahisa; Sano, Yuji*

Metals, 9(11), p.1192_1 - 1192_13, 2019/11

AA2019-0690.pdf:3.91MB

https://doi.org/10.3390/met9111192

The purpose of the present study was to verify the effectiveness of dry laser peening (DryLP), which is the peening technique without a sacrificial overlay under atmospheric conditions using femtosecond laser pulses on the mechanical properties such as hardness, residual stress, and fatigue performance. After DryLP treatment of the laser-welded 2024 aluminum alloy, the softened weld metal recovered to the original hardness of base metal, while residual tensile stress in the weld metal and heat-affected zone changed to compressive stresses. The fatigue life almost doubled at a stress amplitude of 180 MPa and increased by a factor of more than 50 at 120 MPa. As a result, DryLP was found to be more effective for improving the fatigue performance of laser-welded aluminum specimens with welding defects at lower stress amplitudes.