Kihara, Yoshiyuki; Seki, Masayuki; Fujio, Ishibashi,; Hirako, Kazuhiko*; Tsukada, Tatsuya*
JNC TN8430 2005-002, 27 Pages, 2005/07
The irradiation test to gather the creep rupture data of the MARICO-2 test pieces manufactured from Oxide Dispersion Strengthened steel (ODS steel) cladding tube in JFY 2004. Therefore, to improve the reliability of the strength evaluation of the ODS steel cladding tube, it was planned to supplement the creep rupture data in that had been obtained so far. The strength evaluation test pieces supplied to this examination was manufactured by the request of the JNC OEC system nuclear fuel engineering group. This test pieces were manufactured by using Martensitic ODS and Ferritic ODS as well as MARICO-2 and CMIR-6. The specification of the test piece was same as two steel types. The problem did not occur for manufacturing the test pieces (20 pices of Martensitic ODS and 12 pices of Ferritic ODS) from April 5, 2005 to May 13, 2005. It was provided for JNC OEC System Division nuclear fuel group at the May, 2005.
Kono, Shusaku; Seki, Masayuki; Fujio, Ishibashi,; Hirako, Kazuhiko*; Tsukada, Tatsuya*
JNC TN8430 2003-010, 28 Pages, 2003/07
The defect occurred at the resistance welding zone is very minute and therefore cannot be identified by X-ray inspection. Then, the ultrasonic examination method, in which the resolution of the defect is higher than that of the X-ray inspection method, has been developed. The ultrasonic wave sounds straight easier in the material than X rays, excels in defecting the micro defect. However, the pulse amplitude of ultrasonic wave is influenced by the shape and direction of the defect. Then, the ultrasonic inspection equipement, in which the ultrasonic probe and the sample rotation axis are controlled to drive with the pulse motor and the defect data (position and size)are analized by image processing ultrasonic signal, was developed to measure the shape and the position of defect accurately. However, an ultrasonic examination method is the comparative inspection method. Therefore, the standard test block or the reference block is indispensable to guarantee the defectability and the ultrasonic echo sensibility of the inspection device. The standard test block is provided in JIS etc, it is needed to defect the peculiar defect occurred at the resistance welding zone. Then, the method of processing a standard test block is examined, the standard test block was made experimentally by electric discharge processing and diffusion junction method. The ultrasonic echo sensitivity and the threshold for image processing were proofread by using the standard test block, the ultrasonic inspection and metallographic inspection were executed. Comparing the ultrasonic inspection results with the metallographic inspection results, the detectability of defect depth and the measurement accuracy were proved to be 3m and with errors less than 10m respectively. From these results, the effectireness of proofreading the ultrasonic inspection condition by the standard test block was confirmed. Moreover, it was confirmed that there was a peculiar relationship between the depth ...