Sn wires with and without Cu-Nb reinforcement中本 美緒*; 菅野 未知央*; 荻津 透*; 杉本 昌弘*; 谷口 諒*; 廣瀬 清慈*; 川崎 卓郎; Gong, W.; Harjo, S.; 淡路 智*; et al.
IEEE Transactions on Applied Superconductivity, 34(5), p.8400806_1 - 8400806_6, 2024/08
被引用回数：1 パーセンタイル：10.70(Engineering, Electrical & Electronic)For an accelerator magnet, a certain mechanical strength is required to sustain against a transverse compression stress due to Lorentz force. A bronze-route NbSn wire with Cu-Nb reinforcement was developed by Tohoku University and Furukawa Electric to enhance the strength against axial tension. The Cu-Nb reinforcement wire also exhibited some indication of strength improvement against transverse compression; however, the details of a reinforcement mechanism for the transverse compression stress have not been clarified. In this study, the internal strains of NbSn bronze-route wires with and without the Cu-Nb reinforcement under transverse compression stress were evaluated by neutron diffraction at BL19 (TAKUMI) in J-PARC. The samples were attached to jig with solder only at the ends and compression was applied at the center of the samples with 30-mm anvil with 5-mm wide and 8- to 15-mm high beam. Since a critical current, Ic of a superconducting wire depends on the three-dimensional strain, internal strain of NbSn along the axial and two orthogonal radial directions were evaluated at room temperature (RT). In the different setup, Ic measurements of the wires under transverse compression stresses were also performed at 4.2 K and 14.5 T. Using 3-mm wide anvil, the transverse compression was applied at 4.2 K or RT. The neutron diffraction results indicated no significant differences in the internal strains of NbSn under transverse compression between the samples with and without Cu-Nb reinforcement, while the Ic measurements showed potential increase in the irreversible stress (
) for Cu-Nb reinforced wires. The reason for this discrepancy was discussed based on the difference in the experimental setups for each measurement.
山崎 悟志*; 廣瀬 清慈*; 佐々木 宏和*; 大場 洋次郎; 宮澤 知孝*; 大沼 正人*
銅と銅合金, 60(1), p.315 - 319, 2021/08
銅合金においては高強度と高導電性の両立が求められており、これを満たす材料の一つとして、Cu-Ni-Si系合金が知られている。Cu-Ni-Si系合金では、熱時効によりCu母相中にNi-Si系化合物を微細に析出させ、析出強化をもたらすことができるため、このNi-Si粒子の形態が特性にとって重要な役割を果たしている。そこで本研究では、走査型透過電子顕微鏡(STEM)、熱時効中その場X線小角散乱(SAXS)測定、X線吸収微細構造(XAFS)測定により、Ni-Si粒子の観察を行った。その結果、時効中にNi-Si粒子が形成し、粗大化する過程の観察に成功した。
佐々木 宏和*; 西久保 英郎*; 西田 真輔*; 山崎 悟志*; 中崎 竜介*; 磯松 岳己*; 湊 龍一郎*; 衣川 耕平*; 今村 明博*; 大友 晋哉*; et al.
古河電工時報, (138), p.2 - 10, 2019/02
電子顕微鏡や放射光等の先端解析技術は、試料の構造や化学状態について多くの有用な情報をもたらし、材料研究に欠かせないツールとなっている。本稿では、これらの先端解析技術の中から、電子線ホログラフィや放射光を用いたX線小角散乱法(SAXS)等の手法を中心に、材料研究への応用事例を紹介する。これらの手法を活用することにより、未知であった材料の本質を明らかにすることができ、新製品開発の指針を定める上で重要な知見を得ることができる。
山崎 悟志*; 廣瀬 清慈*; 佐々木 宏和*; 大場 洋次郎; 宮澤 知孝*; 大沼 正人*
no journal, ,
電子機器の小型軽量化や高性能化に伴い、リードやコネクタに使用される銅合金には強度および導電性の両立が求められている。Cu-Ni-Si合金は、このような要求を満たす材料として注目されており、Ni-Si系化合物を熱処理によって微細に析出させることにより、高い強度を達成している。したがって、さらなる高性能な材料を開発するためには、Ni-Si系化合物の析出メカニズムを明らかにし、熱処理条件を最適化することが重要である。そこで本研究では、X線小角散乱法により、Cu-Ni-Si合金の熱処理中のその場測定を行った。その結果、Ni-Si系化合物の生成と粗大化を観察することに成功し、熱処理条件の最適化に関する知見を得た。