伊東 達矢; 小川 祐平*; Gong, W.; 川崎 卓郎; 柴田 曉伸*; Harjo, S.
Scripta Materialia, 273, p.117084_1 - 117084_6, 2026/03
The effect of solute hydrogen on stacking fault evolution in austenitic steels remains debated. In this study, the changes in stacking fault probability in the 
111
//loading direction grains family (
) of hydrogen-charged and non-charged Fe-24Cr-19Ni austenitic steels were evaluated using 
neutron diffraction during tensile deformation at 223 and 177 K. When values were plotted against macroscopic strain, hydrogen apparently enhanced stacking fault evolution. However, when identical data were translated into the form of versus stress, the superficial hydrogen-effect on notably disappeared. Rather, deformation temperature played more predominant role - lower temperature led to higher regardless of hydrogen-charging, reflecting the reduction of stacking fault energy with decreasing temperature. These findings demonstrate that hydrogen has a minor effect on stacking fault evolution compared with temperature and applied stress.
Su, Y. H.; 篠原 武尚; Parker, J. D.*; 及川 健一; 甲斐 哲也; Gong, W.; 伊東 達矢; Harjo, S.; 相澤 一也; 鬼柳 善明*; et al.
Materials Science & Engineering A, 951, p.149607_1 - 149607_16, 2026/01
被引用回数：0 パーセンタイル：0.00(Nanoscience & Nanotechnology)Local variations in residual stress/strain and microstructure during fatigue crack growth in compact tension specimens of SUS304 austenitic stainless steel were investigated using complementary methods: pulsed neutron Bragg-edge imaging (NBEI), neutron diffraction (ND), digital image correlation (DIC) and electron backscatter diffraction (EBSD). Surface strain fields were evaluated using DIC and EBSD. NBEI provided two-dimensional averaged microstructure information, whereas ND yielded detailed three-dimensional distributions of residual lattice (elastic) strain and stress. This study particularly focused on how NBEI is helpful in understanding overall damage characteristics in the vicinity of a crack tip two-dimensionally. Distribution of microstructural parameters associated with crack growth, such as lattice constant, crystallite size, and texture, across the entire specimen was considered using Bragg-edge spectral analysis. The plastic zone in front of the crack tip, characterized by reduced crystallite size, was observed during crack propagation. After final fracture, two distinct zones with reduced crystallite size were identified: one caused by localized plastic deformation near the crack tip, and the other by bending at the back end of the specimen. This paper introduces the four experimental techniques and describes their respective features. Each method has its own advantages and limitations; However, by integrating their results, a more comprehensive understanding of the overall stress/strain field can be achieved.
浅森 浩一; 末岡 茂; 小松 哲也; 小形 学; 内田 真緒; 西山 成哲; 田中 桐葉; 小林 智晴; 三ツ口 丈裕; 村上 理; et al.
JAEA-Review 2025-035, 29 Pages, 2025/10
JAEA-Review-2025-035.pdf:1.12MB
本計画書では、高レベル放射性廃棄物の地層処分技術に関する研究開発のうち、深地層の科学的研究の一環として実施している地質環境の長期安定性に関する研究について、第4期中長期目標期間(令和4年度
令和10年度)における令和7年度の研究開発計画を取りまとめた。本計画の策定にあたっては、これまでの研究開発成果や大学等で行われている最新の研究成果に加え、地層処分事業実施主体や規制機関等の動向を考慮した。研究の実施にあたっては、地層処分事業における概要・精密調査や国の安全規制に対し研究成果を適時反映できるよう、(1)調査技術の開発・体系化、(2)長期予測・影響評価モデルの開発、(3)年代測定技術の開発の三つの枠組みで研究開発を推進する。
伊東 達矢; 小川 祐平*; Gong, W.; Mao, W.*; 川崎 卓郎; 岡田 和歩*; 柴田 曉伸*; Harjo, S.
波紋, 35(3), p.129 - 133, 2025/08
Recent studies have shown that the addition of hydrogen to SUS310S stainless steel (Fe-24Cr-19Ni, mass%) simultaneously enhances both strength and ductility, indicating a phenomenon contrary to the conventional understanding of hydrogen embrittlement. In this study, we investigated the underlying mechanism through neutron diffraction experiments during tensile deformation using TAKUMI at the MLF of J-PARC. The results revealed that solid-solution strengthening by hydrogen plays the most significant role in improving the mechanical properties. Solute hydrogen atoms distort the lattice to suppress dislocation motion, thereby increasing the strength. The raised stress in the hydrogen charged sample enables the onset of deformation twinning at a smaller strain compared to the non-hydrogen charged sample. Consequently, the twinning-induced plasticity effect contributes more significantly to work hardening and the improvement of uniform elongation due to the solid-solution strengthening by hydrogen. These findings suggest a new pathway for the effective utilization of hydrogen in austenitic steels.
伊藤 あゆみ*; 菅野 辰哉*; 岩間 崇之*; 植田 滋*; 佐藤 拓未; 永江 勇二
Annals of Nuclear Energy, 217, p.111333_1 - 111333_14, 2025/07
被引用回数：2 パーセンタイル：68.76(Nuclear Science & Technology)福島第一原子力発電所2号機では、原子炉圧力容器の破損に寄与するメカニズムとして、主にFeとZrからなる金属プールの形成が提唱されている。本研究では、炉内劣化過程の後期に金属プールが形成された炉心劣化初期の材料相互作用に着目した。まず、Fe-87ZrとFe-15Zr(at%)の2種類の組成物を液相線温度1723Kまで加熱し、より低温のSS上に滴下し、反応生成物の金属組織を調べた。その後、1723Kから1873KのFe-87Zr融体を酸化SS上に滴下し、酸化膜が劣化に及ぼす影響を評価した。この研究により、すべての金属間化合物の液相線温度が2000K以下であることが確認され、金属破片が最近のシビアアクシデント解析で予測されている「金属プールの形成」の原因となりうることがわかった。
Mao, W.*; Gong, W.; 川崎 卓郎; Gao, S.*; 伊東 達矢; 山下 享介*; Harjo, S.; Zhao, L.*; Wang, Q.*
Scripta Materialia, 264, p.116726_1 - 116726_6, 2025/07
被引用回数：0 パーセンタイル：0.00(Nanoscience & Nanotechnology)An ultrafine-grained 304 austenitic stainless steel exhibited pronounced serrated Luders deformation at 20 K, with stress and temperature oscillations reaching 200 MPa and 20 K. 
neutron diffraction and digital image correlation revealed discontinuous Luders band propagation and burst martensite formation. During deformation, austenite phase stress remained lower than at upper yielding, indicating elastic behavior. Notably, martensite phase stress stayed lower than austenite until fracture, likely due to stress relaxation from burst martensitic transformation at 20 K. The low martensite stress delayed brittle fracture until austenite plastically yielded during uniform deformation.
伊東 達矢; Xu, S.*; Xu, X.*; 大森 俊洋*; 貝沼 亮介*
Shape Memory and Superelasticity, 11(2), p.167 - 175, 2025/06
The microstructure, crystal structures, cold workability, and martensitic transformation temperatures of several Cu
Mn
Al
(40 
55; 10 
13; at%) alloys were analyzed. For the first time, martensitic transformation was revealed Mn-rich Cu-Mn-Al alloys. The surface relief of the martensite phase reversibly appeared and disappeared during cooling and heating, along with small thermal hysteresis, implying a thermoelastic transformation. The crystal structures of the parent and martensite phases are B2 and 2M(BCT), respectively, with c
Mn
Al
(at%) sample. This alloy demonstrates moderate cold workability and cost-effectiveness, exhibiting potential as an alternative for conventional shape memory alloys in various applications.
neutron diffraction study伊東 達矢; 小川 祐平*; Gong, W.; Mao, W.*; 川崎 卓郎; 岡田 和歩*; 柴田 曉伸*; Harjo, S.
Acta Materialia, 287, p.120767_1 - 120767_16, 2025/04
被引用回数：12 パーセンタイル：96.33(Materials Science, Multidisciplinary)Incorporating solute hydrogen into Fe-Cr-Ni-based austenitic stainless steels enhances both strength and ductility, providing a promising solution to hydrogen embrittlement by causing solid-solution strengthening and assisting deformation twinning. However, its impacts on the relevant lattice defects evolution (
, dislocations, stacking faults, and twins) during deformation remains unclear. This study compared the tensile deformation behavior in an Fe-24Cr-19Ni (mass%) austenitic steel with 7600 atom ppm hydrogen-charged (H-charged) and without hydrogen-charged (non-charged) using neutron diffraction. Hydrogen effects on the lattice expansion, solid-solution strengthening, stacking fault probability, stacking fault energy, dislocation density, and strain/stress for twin evolution were quantitatively evaluated to link them with the macroscale mechanical properties. The H-charged sample showed improvements in yield stress, flow stress, and uniform elongation, consistent with earlier findings. However, solute hydrogen exhibited minimal influences on the evolution of dislocation and stacking fault. This fact contradicts the previous reports on hydrogen-enhanced dislocation and stacking fault evolutions, the latter of which can be responsible for the enhancement of twinning. The strain for twin evolution was smaller in the H-charged sample compared to the non-charged one. Nevertheless, when evaluated as the onset stress for twin evolution, there was minimal change between the two samples. These findings suggest that the increase in flow stress due to the solid-solution strengthening by hydrogen is a root cause of accelerated deformation twinning at a smaller strain, leading to an enhanced work-hardening rate and improved uniform elongation.
伊藤 辰也; 永石 隆二; 桑野 涼*; 神戸 正雄*; 吉田 陽一*
Radiation Physics and Chemistry, 226, p.112198_1 - 112198_5, 2025/01
被引用回数：0 パーセンタイル：0.00(Chemistry, Physical)近年、放射線照射実験や非密封放射性同位元素実験用の容器として、ポリイミドやポリエーテルエーテルケトンなどの耐放射線性樹脂の使用が増えている。しかし、水の分解生成物と樹脂との相互作用の可能性が見つかり、樹脂が放射線場における水中の反応に影響を及ぼすことが懸念された。その相互作用を明らかにするために、
線による水の放射線分解における重クロム酸イオン(Cr
O
)の還元と過酸化水素(HO)の生成を樹脂の有無で比較した。同一線量で樹脂ありの水溶液中のCrO還元量は樹脂なしの場合よりも大きくなり、樹脂によってCrO還元が促進されることを示した。一方、電子捕捉剤の有無にかかわらず、純水中のHO生成は樹脂の有無にほとんど依存しなかった。これらは、放射線場において水と接触した樹脂とヒドロキシルラジカルとの相互作用を示唆している。
山本 勝宏*; 今井 達也*; 河合 純希*; 伊藤 恵利*; 宮崎 司*; 宮田 登*; 山田 悟史*; 瀬戸 秀紀*; 青木 裕之
ACS Applied Materials & Interfaces, 16(48), p.66782 - 66791, 2024/11
被引用回数：1 パーセンタイル：10.77(Nanoscience & Nanotechnology)In this study, a silicon-based copolymer, poly(tris(trimethylsiloxy)-3-methacryloxypropylsilane)-co-poly(N,N-dimethyl acrylamide), thin film was subjected to plasma surface treatment to make its surface hydrophilic (biocompatible). Neutron reflectivity (NR) measurement of the plasma-treated thin film showed a decrease in the film thickness (etching width: similar to 20 nm) and an increase in the scattering length density (SLD) near the surface (similar to 15 nm). The region with a considerably high SLD adsorbed water (DO) from its saturated vapor, indicating its superior surface hydrophilicity. Nevertheless of the hydrophilicity, the swelling of the thin film was suppressed. Hard X-ray photoelectron spectroscopy (HAXPES) performed at various takeoff angles revealed that the thin-film surface (similar to 20 nm depth) underwent extensive oxidation. NR and HAXPES analysis quantitatively yielded the depth profiling of elemental compositions in a few tens of nm scale. Si oxidation and hydrogen elimination (probably CH
groups) in the vicinity of the surface region increased the SLD and decreased the hydrophobicity. A combination of Soft X-ray photoelectron spectroscopy and NR measurements revealed the surface chemical composition and mass density. It was considered that the surface near the film was chemically composed close to SiO, forming a gel-like (three-dimensional network) structure that is hydrophilic and suppresses swelling due to moisture, indicating it can be expected to maintain stable hydrophilicity on the film surface.
neutron diffraction study to elucidate hydrogen effect on the deformation mechanism in Type 310S austenitic stainless steel伊東 達矢; 小川 祐平*; Gong, W.; Mao, W.*; 川崎 卓郎; 岡田 和歩*; 柴田 曉伸*; Harjo, S.
Proceedings of the 7th International Symposium on Steel Science (ISSS 2024), p.237 - 240, 2024/11
Hydrogen embrittlement has long been an obstacle to the development of safe infrastructure. However, in contrast to hydrogen's embrittling effect, recent research has revealed that the addition of hydrogen improves both the strength and uniform elongation of AISI Type 310S austenitic stainless steel. A detailed understanding of how hydrogen affects the deformation mechanism of this steel could pave the way for the development of more advanced materials with superior properties. In the present study, neutron diffraction experiments were conducted on Type 310S steel with and without hydrogen-charged to investigate the effect of hydrogen on the deformation mechanism. In addition to the effect of solid-solution strengthening by hydrogen, the q-value, a parameter representing the proportion of edge and screw dislocations in the accumulated dislocations, was quantitatively evaluated using CMWP analysis on neutron diffraction patterns. The comparison of q-values between the hydrogen-charged and non-charged samples reveals that hydrogen has minimal effect on dislocation character in Type 310S steel.
Mao, W.*; Gao, S.*; Gong, W.; 川崎 卓郎; 伊東 達矢; Harjo, S.; 辻 伸泰*
Acta Materialia, 278, p.120233_1 - 120233_13, 2024/10
被引用回数：33 パーセンタイル：98.21(Materials Science, Multidisciplinary)Using a hybrid method of in situ neutron diffraction and digital image correlation, we found that ultrafine-grained 304 stainless steel exhibits Luders deformation after yielding, in which the deformation behavior changes from a cooperation mechanism involving dislocation slip and martensitic transformation to one primarily governed by martensitic transformation, as the temperature decreases from 295 K to 77 K. Such martensitic transformation-governed Luders deformation delays the activation of plastic deformation in both the austenite parent and martensite product, resulting in delayed strain hardening. This preserves the strain-hardening capability for the later stage of deformation, thereby maintaining a remarkable elongation of 29% while achieving a high tensile strength of 1.87 GPa at 77 K.
中島 多朗*; 齋藤 開*; 小林 尚暉*; 川崎 卓郎; 中村 龍也; 古川 はづき*; 浅井 晋一郎*; 益田 隆嗣*
Journal of the Physical Society of Japan, 93(9), p.091002_1 - 091002_5, 2024/09
被引用回数：2 パーセンタイル：42.44(Physics, Multidisciplinary)Neutron scattering is a powerful tool to study magnetic structures and cross-correlated phenomena originated from symmetry of the magnetic structures in matter. Among a number of neutron scattering techniques, polarized neutron scattering is quite sensitive to the orientations of the magnetic moments, which are essential to understand microscopic mechanisms of the spin-driven emergent phenomena. Here, we present POlarized Neutron Triple-Axis spectrometer PONTA in the Japan Research Reactor 3 (JRR-3), and show the present capabilities of polarized and unpolarized neutron scattering by introducing recent results from the instrument.
-dioctylthiodiglycolamic acid; Effect of S donor on metal extraction下条 晃司郎; 藤原 伊織*; 斉藤 拓巳*; 大島 達也*
Analytical Sciences, 40(8), p.1429 - 1436, 2024/08
被引用回数：0 パーセンタイル：0.00(Chemistry, Analytical)アミド基とカルボン酸をチオエーテル鎖で結合したソフトベース硫黄ドナー配位子である-ジオクチルチオジグリコール酸(T-DODGAA)を用いて56種類の金属イオンの抽出能力が包括的に調査し、エーテル性酸素原子よりなるハードベースドナー配位子であるN, N-ジオクチルジグリコール酸(DODGAA)との抽出能力を比較した。チオジグリコール酸骨格のp
は、電位差滴定により水(0.1M LiCl、25
C)中で3.71
0.06と算出され、これは、T-DODGAAがDODGAA (p = 3.540.03)よりわずかに弱い酸であることを示す。T-DODGAAはプロトン交換反応により56種類の金属イオンから様々な金属イオンを定量的に抽出することができる。T-DODGAAは、Hf(IV)、Cr(III)、Fe(III)、Ni(II)、Cu(II)、Pd(II)、Ag(I)、Au(III)、Hg(II)、Al(III)、Ga(III)、特にソフト金属イオンにたいして高い抽出能を有する。さらに、湿式製錬や金属リサイクルにおけるT-DODGAAの実用可能性を実証するために、金属混合抽出システムにおけるSc(III)、Ni(II)、Co(II)、Pd(II)、Au(III)、In(III)およびGa(II)のようなレアメタルの選択的分離実験を行った。
伊藤 辰也; 永石 隆二; 桑野 涼*
Nuclear Technology, 210(8), p.1427 - 1443, 2024/08
被引用回数：0 パーセンタイル：0.00(Nuclear Science & Technology)福島第一原子力発電所の多核種除去設備における凝集沈殿(共沈)プロセスから排出される放射性廃棄物のような強アルカリ条件下で、水の放射線分解によって発生した水素(H)気泡の保持を、マグネシウムとカルシウムの混合沈殿物である懸濁物固体(SS)からなる炭酸塩スラリーの高粘度懸濁液中で定量的に研究した。親水性の異なる2種類の炭酸塩スラリー、親水性の「現行型」と疎水性の「返送型」についてH保持特性を評価し、それらの特性を別の懸濁液であるベントナイトの粘土懸濁液の特性と比較した。SS粒子表面の化学吸着量とスラリー中のHOの量の比較から、SS粒子間でHO分子が共有されている必要があり、この共有により粘土懸濁液中で微細な粘土鉱物間の静電的な結合が形成する粘性とは異なる構造粘性が形成されることが確認された。スラリー中のH気泡の保持は、
Co線照射後のスラリーの撹拌前後で観測されたH発生量の差から評価した。親水性スラリー、疎水性スラリー、粘土懸濁液、処理水の保持特性の比較から、親水性スラリー中のH気泡は構造粘性だけでなく立体障害によっても保持されると示唆された。
服部 高典; 鈴木 浩二*; 三代 達也*; 伊藤 崇芳*; 町田 真一*
Nuclear Instruments and Methods in Physics Research A, 1064, p.169448_1 - 169448_9, 2024/07
被引用回数：0 パーセンタイル：0.00(Instruments & Instrumentation)著者らは、抄録と要約で標準的なダブルトロイダルアンビルのカップ径が1.5mmであると説明していることを遺憾に思う。これは誤りで、標準的な直径は4.0mmである。ご迷惑をおかけしたことをお詫びする。
Si今 布咲子*; 田端 千紘; 齋藤 開*; 中島 多朗*; 日高 宏之*; 柳澤 達也*; 網塚 浩*
Journal of the Physical Society of Japan, 93(4), p.044701_1 - 044701_11, 2024/04
被引用回数：1 パーセンタイル：24.78(Physics, Multidisciplinary)We investigated the magnetic structure of the antiferromagnetic (AFM) ordered state (
34 K) in tetragonal UPtSi using polarized and unpolarized neutron diffraction. Previous neutron scattering studies reported that this system possesses a simple AFM structure with a propagation vector, Q= 0, and the ordered magnetic moments aligned along the c-axis. By contrast, our latest resonant X-ray scattering (RXS) experiments have revealed that the magnetic structure is modulated by the charge-density-wave (CDW) order, which emerges in one of the two Pt atomic layers in the unit cell below 320 K. The modulation is characterized by a transverse wave in the c-plane, with the propagation vector of the CDW order, q
= (0.42, 0, 0). In this study using neutron scattering, we observed that the superlattice reflections specified by q develop below , in addition to the magnetic reflections with Q= 0, thereby further confirming the presence of modulation in the AFM structure of this system. From detailed analyses, we revealed that the amplitude of the transverse-wave magnetic modulation is 0.72(2)
/U, which is quantitative information that can not be obtained through RXS experiments. This implies that the CDW drives the ordered magnetic moments to be tilted up to 20 in the AFM state. The observations strongly suggest that the magnetism of UPtSi is heavily influenced by the hybridization effects between the 
electrons of U and the 5d electrons of Pt.
大沢 直樹*; Kim, S.-Y.*; 久保田 真彦*; Wu, H.*; 渡部 創; 伊藤 辰也; 永石 隆二
Nuclear Engineering and Technology, 56(3), p.812 - 818, 2024/03
被引用回数：4 パーセンタイル：65.33(Nuclear Science & Technology)An impregnated silica-based adsorbent was prepared by combining HONTA extractant, Crea extractant, and macroporous silica polymer composite particles (SiO-P). The performance of platinum-group metals adsorption and separation on prepared (HONTA + Crea)/SiO-P adsorbent was assessed by batch-adsorption and chromatographic separation studies. (HONTA + Crea)/SiO-P adsorbent showed high adsorption performance of Pd(II) owing to an affinity between Pd(II) and Crea extractant based on the Hard and Soft Acids and Bases theory. The chromatographic experiment showed that Pd(II) was recovered entirely from the feed solution using 0.2 M thiourea in 0.1 M HNO. Possibility of recovery of Zr(IV), Mo(VI), and Re(VII) was also observed using the (HONTA + Crea)/SiO-P adsorbent.
Re in the keV energy region片渕 竜也*; 佐藤 八起*; 武部 花凛*; 井頭 政之*; 梅澤 征悟*; 藤岡 諒*; 齋藤 辰宏*; 岩本 信之
Journal of Nuclear Science and Technology, 61(2), p.224 - 229, 2024/02
被引用回数：0 パーセンタイル：0.00(Nuclear Science & Technology)Measurements of the neutron capture cross section of Re have been limited in the keV energy region. In addition, existing measured data have discrepancies. In this study, the neutron time-of-flight method was employed to measure the capture cross section of Re at Tokyo Institute of Technology. The capture -rays were detected with a large volume NaI(Tl) detector. The pulse-height weighting technique was applied to obtain the capture yield. The present results were corrected for neutron scattered effects and impurities in the sample. The measured cross sections were determined with the standard capture cross section of gold in the energy range from 15 to 90 keV, and compared with measured and evaluated data. The results of the measurement provided improved accuracy relative to previous studies in the keV energy range.
今富 大介*; 石川 遼典*; 仲田 玲*; 伊東 達矢; Han, K.*; 長迫 実*; Xu, X.*; 大森 俊洋*; 貝沼 亮介*
Journal of Phase Equilibria and Diffusion, 45(1), p.3 - 17, 2024/02
被引用回数：4 パーセンタイル：31.44(Chemistry, Physical)Mn-Zn二元系における相平衡を、組成分析、結晶構造解析、熱分析により実験的に決定した。これまでの報告と比較し、
相、
相、
相の存在領域に違いが見られた。相の領域から急冷した試料でMn相と同じ不規則な体心立方構造が確認されたため、-B2の単相域は確認できなかった。先行研究において、相が,
,
相に分離しているかどうかが論争になっていきたが、拡散対といくつかの合金組成の調査により、相、相、相は分離しておらず、単一の相となっていることが示された。さらに、熱分析によって対応する不変系反応が検出されなかったことから、相はZn過剰領域には存在しない。