荒井 陽一; 渡部 創; 中原 将海; 船越 智雅; 星野 貴紀; 高畠 容子; 坂本 淳志; 粟飯原 はるか; 長谷川 健太; 吉田 稔生; et al.
Progress in Nuclear Science and Technology (Internet), 7, p.168 - 174, 2025/05
STRADプロジェクトの進捗に係る報告として、CPFホットセルの処理状況とともに、新たなターゲットに係る研究計画と最新のトピックスについて報告する。
船越 智雅; 渡部 創; 荒井 陽一; 岩本 敏広; 渡部 雅之; 西本 能弘*; 安田 誠*
Mechanical Engineering Journal (Internet), 11(2), p.23-00445_1 - 23-00445_7, 2024/04
Various types of machine oil are used for analysis and utility equipment, and these organic liquid wastes are stored in nuclear facilities and laboratories. Perfluoro oil, generally used in vacuum pumps, is difficult to decompose because of its chemical stability. In order to achieve complete mineralization of the organic liquid wastes, the application of a subcritical water reaction was examined. In this study, the effect of introducing a functional group into a perfluoro compound on its decomposition performance was experimentally evaluated. First, we carried out the transformation of perfluorohexane to perfluorohexyl iodide or perfluoroheptanoic acid based on reported procedures. Next, laboratory scale batchwise decomposition tests with subcritical water on perfluorohexyl iodide and on perfluoro heptanoic acid were carried out. The decomposition products of each fluorine compound were identified, confirming that subcritical treatment is a promising treatment method.
岩本 敏広; 齋藤 まどか*; 高畠 容子; 渡部 創; 渡部 雅之; 成瀬 惇喜*; 塚原 剛彦*
Mechanical Engineering Journal (Internet), 11(2), p.23-00444_1 - 23-00444_7, 2024/04
Nuclear fuel fabrication process has generated a large amount of wastes contaminated with enriched uranium, and those have been accumulated for long time in Japan. These waste hasn't treated, because there is no protocol to treat and dispose these. Procedure is proposed; 1) Leaching Uranium from the waste, 2) recovering uranium from the leaching solution, 3) treating residue and secondary waste for disposing in the near field region. Temperature swing extraction technology is one of promising methods to recover uranium efficiently. In the technology, uranium ions are extracted by extraction, and complex with ligands are separated by a polymer with reversible hydrophilic-hydrophobic properties. Monoamides can be adopted to the procedure. However suitable structure of monoamide for the technology is unclear. Therefore, for deciding appropriate structure of monoamides, these with different alkyl chain structures were synthesized, and applicability of the extractants were evaluated by solvent extraction and temperature swing extraction experiments. In experiments, Ce(IV) was used as a simulant of U(IV). Three monoamides were synthesized, and solvent extraction experiments and Temperature swing extraction experiments were carried out.
岩本 敏広; 齋藤 まどか*; 高畠 容子; 渡部 創; 渡部 雅之; 成瀬 惇喜*; 塚原 剛彦*
Proceedings of 30th International Conference on Nuclear Engineering (ICONE30) (Internet), 4 Pages, 2023/05
モノアミド抽出剤と温度応答性ポリマーを用いたゲル化抽出技術のウラン廃棄物処理への適用性の検討を行った。異なる構造を有する3種類のモノアミド抽出剤を用いた模擬溶液の分離試験により、溶液中のCe(IV)をゲル化抽出法により選択的に回収されることが示された。これらの試験結果をもとに、ゲル化抽出法に適したモノアミド抽出剤を選定した。
甲斐 正雄; 岩本 敏広; 齋藤 まどか*; 高畠 容子; 渡部 創; 中村 雅弘; 塚原 剛彦*; 井戸田 直和*; 成瀬 惇喜*
no journal, ,
軽水炉燃料加工時にウランを含むスラッジが各施設で発生し、保管されている。保管されているスラッジからウランを浸出させた溶液から、ウランを選択回収する。ウランの選択回収にはゲル化抽出法を選択した。本検討では、ゲル化抽出法にて回収したゲル試料について、適した酸化転換手法を求めるために、電気炉を用いた酸化転換法の検討を実施した。まずセリウムにて検討を実施した。異なる温度で回収ゲルを加熱し、その性状を分析した。結果、加熱温度として1000
Cが適当との結果が得られた。次に、硝酸ウラニルを用いて作製したゲルを1000Cにて加熱し、得られた試料について分析を行った。発表では、分析に基づく試料の同定結果について報告を行う。
甲斐 正雄; 佐藤 隆宣*; 岩本 敏広; 齋藤 まどか*; 中原 将海; 高畠 容子; 渡部 創; 中村 雅弘; 成瀬 惇喜*; 井戸田 直和*; et al.
no journal, ,
燃料加工施設においてウランを含むスラッジ廃棄物が発生している。このスラッジ廃棄物を硝酸に浸出させて溶液中のウランの選択的回収を行う。ウランの選択的回収にはゲル化抽出法を選択した。本研究では、ゲル化抽出技術の実用化のために小型の試験装置を開発し、撹拌性能やゲルを含む溶液の移送、ゲルの分離を実験的に調べた。ウランの模擬物質としてセリウム(IV)を使用してゲル化抽出を行い、ゲル溶液を効率的に撹拌し、回収しやすい撹拌翼を選定した。また、ゲル溶液は自給式のポンプを使用することで移送可能であること、遠心脱水機でゲルと溶液を分離できることを確認した。
高畠 容子; 齋藤 まどか*; 岩本 敏広; 渡部 創; 渡部 雅之
no journal, ,
軽水炉燃料加工時にウランを含むスラッジが各施設で発生し、保管されている。保管されているスラッジからウランを浸出させた溶液から、ウランを選択回収する。本検討では、スラッジ浸出液を処理する工学規模設備の実現に向けて、ウラン回収方法の市場調査を行った。候補手法を設備規模,二次廃棄物量,手法の成熟度,長所,短所の観点から比較し、今後検討すべき技術の選出とともに、研究開発計画を立案した。
岩本 敏広; 齋藤 まどか*; 高畠 容子; 渡部 創; 渡部 雅之; 成瀬 惇喜*; 塚原 剛彦*
no journal, ,
軽水炉燃料加工時にウランを含むスラッジが各施設で発生し、保管されている。保管されているスラッジからウランを浸出させた溶液から、ウランを選択回収する。ウランの選択回収にはゲル化抽出法を選択し、それに適した抽出剤を2種選択し、セリウムにて実験を行い、その性能を評価した。C14-BAMAが優れているとの結果が得られたため、当該抽出剤に対してウランによる検討を行う予定である。