Kanayama, Hideyuki*; Hiyoshi, Noritake*; Ogawa, Fumio*; Kawabata, Mie*; Ito, Takamoto*; Wakai, Takashi
Zairyo, 68(5), p.421 - 428, 2019/05
This study presents creep damage assessment method for Mod. 9Cr-1Mo steel by sampling creep testing with thin plate specimen. Tensile creep rupture tests were performed using three different sizes of specimen under two different test environments to verify the creep testing with the thin plate specimen. Time to rupture of Mod. 9Cr-1Mo steel using three different sizes were almost same. In addition, there was no effect of environment on time to rupture. Pre-damaged thin plate specimens were machined from a bulk specimen's gage section that pre-damage test was performed with. Pre-damage based on life fraction rule were 8%, 16% and 25%. No effect of the process of machining pre-damaged specimen on time to rupture was confirmed by verification tests in same test condition as pre-damage test. Stress acceleration creep rupture tests were performed to estimate creep damage assessment. Creep damage assessment by stress acceleration creep rupture tests was sufficiently accurate estimate. Creep damage assessments by Vickers hardness and lath width were compared with the assessment by stress acceleration creep rupture tests to study applicability of these methods.
Kanayama, Hideyuki; Hiyoshi, Noritake*; Ito, Takamoto*; Ogawa, Fumio*; Wakai, Takashi
Zairyo, 66(2), p.86 - 92, 2017/02
This study presents creep characteristics of Mod. 9Cr-1Mo steel with various sized specimens and environment. Creep tests were performed using three different sizes of specimen and three different type of testing environment. Specimens are a bulk specimen which has 6mm diameter and 30mm gage length, a miniature specimen which has 2mm diameter and 10mm gage length and a thin plate specimen which has 0.76mm thickness, 1.5mm width and 7.62mm gage length. Three different type of testing environment are air, 99.99% Ar gas and vacuum. In the same environmental condition, there was no effect of specimen size on time to rupture. Time to rupture of Mod. 9Cr-1Mo steel in Ar gas was shorter than that in air and vacuum. Oxide thickness is not dominant factor in time to rupture. Fracture mode at specimen surface in Ar gas might be dominant factor in shorter time to rupture. Effect of specimen size and environment on creep strength of Mod. 9Cr-1Mo steel was evaluated on the basis of thinning.
Kanayama, Hideyuki; Nagae, Yuji; Onizawa, Takashi; Wakai, Takashi; Imo, Kazumichi*
no journal, ,
no abstracts in English
Kanayama, Hideyuki; Hiyoshi, Noritake*; Ogawa, Fumio*; Ito, Takamoto*; Wakai, Takashi
no journal, ,
no abstracts in English