Shinohara, Yasunari*; Abe, Hiroaki*; Iwai, Takeo*; Sekimura, Naoto*; Kido, Toshiya*; Yamamoto, Hiroyuki; Taguchi, Tomitsugu
Journal of Nuclear Science and Technology, 46(6), p.564 - 571, 2009/06
Times Cited Count:31 Percentile:87.07(Nuclear Science & Technology) observation during hydrogen ion implantation was performed with a TEM installed in an ion accelerator to investigate the growth process of Zr hydride in Zicaloy-4. To clarify the effect of radiation damage, some samples were irradiated with 4 MeV Ni
ions prior to hydrogen implantation. Growth processes of Zr hydrides accompanying the formation of dislocations were observed. The crystallographic relationship between the Zr matrix and Zr hydrides was identical with that found in previous studies: inter- and intragranular hydrides exhibiting a tendency to grow in the
11
0
direction. This growth can be attributed to a shear mechanism. In specimens preirradiated with Ni ions, the growth rate of hydrides was suppressed, but the growth direction was not affected by radiation defects. It was also confirmed that the black spots induced by Ni
ion irradiation grew during hydrogen ion implantation, suggesting the formation of hydrides at the defects.
Okubo, Tadatsune*; Tsukuda, Yoshiaki*; Kamimura, Katsuichiro*; Murai, Kenji*; Goto, Ken*; Doi, Soichi*; Senda, Yasuhide*; Kosaka, Yuji*; Kido, Toshiya*; Murata, Tamotsu*; et al.
Nihon Genshiryoku Gakkai-Shi, 43(9), p.906 - 915, 2001/09
Times Cited Count:0 Percentile:0.00(Nuclear Science & Technology)no abstracts in English