光田 智昭*; 小林 一平*; 小杉 晋也*; 藤田 直樹*; 齋藤 勇一; 堀 史説*; 千星 聡*; 金野 泰幸*; 西田 憲二*; 曽根田 直樹*; et al.
Nuclear Instruments and Methods in Physics Research B, 272, p.49 - 52, 2012/02
被引用回数:10 パーセンタイル:58.96(Instruments & Instrumentation)So far, we have found that the hardness of Al-Cu-Mg alloy (JIS2017, Duralumin) increases by energetic heavy ion irradiation at room temperature. Observations by using the three-dimensional atom probe (3DAP) have revealed that nano-meter sized precipitates are homogeneously distributed in the irradiated specimens, which are produced through the irradiation enhanced diffusion of solute atoms. The small precipitates contribute to the increase in hardness. In this report, we show the results for the hardness modification of Al-Cu-Mg alloy by the combination of energetic ion irradiation and thermal aging treatment. The hardness of the specimens pre-irradiated and thermally aged at 423 K is much larger than that without the pre-irradiation. The present result indicates that the combination of energetic ion irradiation and subsequent thermal aging can be used as an effective tool for the hardness modification of Al-Cu-Mg alloy.
光田 智昭*; 小林 一平*; 小杉 晋也*; 藤田 直樹*; 齋藤 勇一; 堀 史説*; 千星 聡*; 金野 泰幸*; 西田 憲二*; 曽根田 直樹*; et al.
Journal of Nuclear Materials, 408(2), p.201 - 204, 2011/01
被引用回数:14 パーセンタイル:70.87(Materials Science, Multidisciplinary)We irradiated Al-Cu-Mg alloy with 10 MeV iodine ions at room temperature and measured the surface microhardness. We analyzed the microstructure using a three-dimensional atom probe. Irradiation for 3.5 h led to an increase in hardness comparable to that obtained after 4 days of aging at 423 K. Precipitates of about 2.9 nm in diameter were distributed homogeneously over the irradiated region. The nanometer-sized precipitates produced by the irradiation caused a remarkable increase in hardness.
光田 智昭*; 岩瀬 彰宏*; 齋藤 勇一
no journal, ,
金属や酸化物材料など無機材料において、高エネルギー荷電粒子ビームを利用した物質改質や創製に取り組んでいる。本研究では、ジュラルミン及び比較のための純アルミニウム金属,アルミニウム-銅2元合金にタンデム加速器からの10MeVヨウ素イオンなどによる照射を行い、照射前後の表面硬度及び微細結晶構造の変化を3次元アトムプローブ等を用いて評価した。その結果、重イオンビームでこの材料を照射すると、室温で2時間の照射により、150C時効の最大値に相当する硬度が得られた。これは、イオン照射促進析出によるナノメートルサイズの微小析出物が生成されたためであることを3次元アトムプローブ観察により明らかにした。また、イオン照射と熱時効を組合せたプロセシングを行うと、さらなる硬度の上昇がみられ、これは、照射によって析出したナノスケール析出物を核として、熱時効により核成長が起ったためであることを3次元アトムプローブ観察により明らかにした。