Application of X-ray photoelectron spectroscopy to characterization of Au nanoparticles formed by ion implantation into SiO

高廣 克己*; 大泉 信之助*; 森本 圭一*; 川面 澄*; 一色 俊之*; 西尾 弘司*; 永田 晋二*; 山本 春也; 鳴海 一雅; 楢本 洋*

Applied Surface Science, 256(4), p.1061 - 1064, 2009/11

https://doi.org/10.1016/j.apsusc.2009.05.104

In X-ray photoelectron spectroscopy (XPS) of Au nanoparticles, the width of 5d valence band changes with Au particle size. This enables us to estimate the size of Au nanoparticles by using XPS. In this work, the 5d-band width has been measured for Au nanoparticles formed by ion implantation into SiO. The 5d-band width is found to be correlated strongly with the Au concentration. As the Au concentration increases, the 5d-band width becomes larger, indicating that the Au nanoparticles with the larger size tend to be formed in the vicinity of the projected range of Au ions. This correlation agrees very well with the results from transmission electron microscopy.

「軽水炉用」プルトニウム富化燃料のHBWR照射試験,8; IFA-565燃料集合体の照射データ及び照射後試験結果報告

上村 勝一郎; 矢野 総一郎; 河野 秀作; 加藤 正人; 森本 恭一; 森平 正之; 菊池 圭一

PNC TN8410 97-067, 452 Pages, 1997/02

PNC-TN8410-97-067.pdf:37.67MB

ハルデン炉において、「軽水炉用」プルトニウム富化燃料(Puf富化度4.6w/o)の高燃焼度照射試験(IFA-565)を実施した。IFA-565は、IFA-514照射試験として照射した6本の燃料棒のうち、3本について同一リグにて継続照射したものである。IFA-514については既報にまとめられており、本報告では、継続照射した照射データ及び照射後試験結果について解析・評価を行った。得られた結果は、以下の5点である。(1)ペレットピーク燃焼度で61GWd/tMOXの高燃焼度まで健全に燃焼すること確認した。(2)FPガス放出挙動はBWRUO2及びATR用のMOX燃料の挙動と類似しており、FPガス放出率に差は認められない。また、中空ペレットのFPガス放出率(13.0%)は中実ペレット(17.3%)より低い。(3)金相観察結果及びペレット長の変形量からいずれの燃料棒にも大きなPCMIは生じておらず、ペレット形状(中実と中空)がPCMI挙動に与える影響に明確な差は認められない。しかし、中空ペレットの方が中実ペレットに比べて燃料棒外径変化率がやや小さく、外径変化の抑制に効果がある。(4)燃料棒の伸びはBWRUO燃料棒及びATR用MOX燃料棒に比べてやや小さく、約0.15%である。(5)製造時に存在したペレットの造粒界が照射中に消失することにより、ペレットスウェリングの緩和に効果のあったことが推察される。