Initialising ...
Initialising ...
Initialising ...
Initialising ...
Initialising ...
Initialising ...
Initialising ...
-spectroscopy at an intense cold neutron beam facilityJentschel, M.*; Blanc, A.*; de France, G.*; K
ster, U.*; Leoni, S.*; Mutti, P.*; Simpson, G.*; Soldner, T.*; Ur, C.*; Urban, W.*; et al.
Journal of Instrumentation (Internet), 12(11), p.P11003_1 - P11003_33, 2017/11
被引用回数：43 パーセンタイル：85.39(Instruments & Instrumentation)A highly efficient array of high-purity germanium (HPGe) detectors was developed and operated at the cold neutron beam facility PF1B of the Institut Laue-Langevin (ILL) to carry out nuclear structure studies, via measurements of -rays following neutron-induced capture and fission reactions. The setup consisted of a collimation system producing a pencil beam with a thermal capture equivalent flux of about 10
ns
cm
at the target position and negligible neutron halo. The target was surrounded by an array of eight to ten anti-Compton shielded EXOGAM Clover detectors, four to six anti-Compton shielded large coaxial GASP detectors and two standard Clover detectors. For a part of the campaign the array was combined with 16 LaBr
:(Ce) detectors from the FATIMA collaboration.
友田 陽*; 徐 平光; Oliver, E. C.*; Paradowska, A.*
In-Situ Studies with Photons, Neutrons and Electrons Scattering, p.175 - 190, 2010/12
Neutron diffraction has been employed to study microstructural evolution in situ during heat treatment or thermo-mechanically controlled process for low alloy steels. Transformation kinetics, texture, carbon enrichment and internal stresses can be tracked and these data are useful to develop new processing to realize optimum microstructures.
徐 平光; 友田 陽*; Li, J.*; Oliver, E. C.*; 足立 吉隆*
no journal, ,
本研究は飛行時間法その場中性子回折を用い、17Ni-0.2C及び2Mn-0.2Cマルテンサイト鋼温間加工中の動的再結晶挙動を調査した。17Ni-0.2C鋼は773K熱間圧縮中にマルテンサイトからオーステナイトへの動的析出が進行し、析出したオーステナイトの加工集合組織が緩やかに増大した。また圧縮初期からマルテンサイトの変形によりフェライトの加工集合組織は強められ、それに加えて特定の歪み量を超えるとフェライトの動的再結晶が起こり集合組織は弱められる。二つの作用のバランスにより最終的な集合組織が形成される。2Mn-0.2C鋼の873K熱間圧縮では、フェライトの動的再結晶はマルテンサイトの回復とセメンタイトの析出によって引き起こされ、17Ni-0.2C鋼より高い歪み領域で開始した。二つマルテンサイト鋼の再結晶挙動の違いは硬質第二相の体積率と関連があると推定した。