Yamaki, Tetsuya; Nuryanthi, N.*; Koshikawa, Hiroshi; Asano, Masaharu; Sawada, Shinichi; Hakoda, Teruyuki; Maekawa, Yasunari; Voss, K.-O.*; Severin, D.*; Seidl, T.*; et al.
Nuclear Instruments and Methods in Physics Research B, 314, p.77 - 81, 2013/11
Times Cited Count:3 Percentile:26.71(Instruments & Instrumentation)Ion-track membranes of poly(vinylidene fluoride) (PVDF), a type of fluoropolymer, could find wide applications due to its superior chemical and mechanical properties. In order to produce track-etched pores in PVDF films, we have independently employed much milder etching conditions without any oxidant additives in the alkaline etching solution. The goal of this work is to pursue the possibility of varying beam parameters and applying the effect of the etching pretreatment to control the pore size and shape. Ongoing in-situ/on-line analyses at the M-branch of the UNILAC would shed light on the detailed chemistry of not only ion-induced degradation but also the post-irradiation reactivity.
Adare, A.*; Afanasiev, S.*; Aidala, C.*; Ajitanand, N. N.*; Akiba, Y.*; Al-Bataineh, H.*; Alexander, J.*; Aoki, K.*; Aphecetche, L.*; Armendariz, R.*; et al.
Physical Review D, 84(1), p.012006_1 - 012006_18, 2011/07
Times Cited Count:29 Percentile:72.31(Astronomy & Astrophysics)We report on the event structure and double helicity asymmetry () of jet production in longitudinally polarized collisions at = 200 GeV. Photons and charged particles were measured by the PHENIX experiment. Event structure was compared with the results from PYTHIA event generator. The production rate of reconstructed jets is satisfactorily reproduced with the next-to-leading-order perturbative QCD calculation. We measured = -0.0014 0.0037 at the lowest bin and -0.0181 0.0282 at the highest bin. The measured is compared with the predictions that assume various distributions.
Adare, A.*; Afanasiev, S.*; Aidala, C.*; Ajitanand, N. N.*; Akiba, Yasuyuki*; Al-Bataineh, H.*; Alexander, J.*; Aoki, Kazuya*; Aphecetche, L.*; Armendariz, R.*; et al.
Physical Review C, 83(6), p.064903_1 - 064903_29, 2011/06
Times Cited Count:184 Percentile:99.44(Physics, Nuclear)Transverse momentum distributions and yields for , and in collisions at = 200 and 62.4 GeV at midrapidity are measured by the PHENIX experiment at the RHIC. We present the inverse slope parameter, mean transverse momentum, and yield per unit rapidity at each energy, and compare them to other measurements at different collisions. We also present the scaling properties such as and scaling and discuss the mechanism of the particle production in collisions. The measured spectra are compared to next-to-leading order perturbative QCD calculations.
Adare, A.*; Afanasiev, S.*; Aidala, C.*; Ajitanand, N. N.*; Akiba, Yasuyuki*; Al-Bataineh, H.*; Alexander, J.*; Aoki, Kazuya*; Aphecetche, L.*; Aramaki, Y.*; et al.
Physical Review C, 83(4), p.044912_1 - 044912_16, 2011/04
Times Cited Count:8 Percentile:49.7(Physics, Nuclear)Measurements of electrons from the decay of open-heavy-flavor mesons have shown that the yields are suppressed in Au+Au collisions compared to expectations from binary-scaled collisions. Here we extend these studies to two particle correlations where one particle is an electron from the decay of a heavy flavor meson and the other is a charged hadron from either the decay of the heavy meson or from jet fragmentation. These measurements provide more detailed information about the interaction between heavy quarks and the quark-gluon matter. We find the away-side-jet shape and yield to be modified in Au+Au collisions compared to collisions.
Adare, A.*; Afanasiev, S.*; Aidala, C.*; Ajitanand, N. N.*; Akiba, Y.*; Al-Bataineh, H.*; Alexander, J.*; Aoki, K.*; Aphecetche, L.*; Armendariz, R.*; et al.
Physical Review D, 83(5), p.052004_1 - 052004_26, 2011/03
Times Cited Count:175 Percentile:98.48(Astronomy & Astrophysics)The PHENIX experiment at RHIC has measured the invariant differential cross section for production of , , and mesons in collisions at = 200 GeV. The spectral shapes of all hadron transverse momentum distributions are well described by a Tsallis distribution functional form with only two parameters, and , determining the high and characterizing the low regions for the spectra, respectively. The integrated invariant cross sections calculated from the fitted distributions are found to be consistent with existing measurements and with statistical model predictions.
Yamaki, Tetsuya; Koshikawa, Hiroshi; Asano, Masaharu; Maekawa, Yasunari; Severin, D.*; Seidl, T.*; Trautmann, C.*
no journal, ,
There has been a strong motivation for us to investigate the detailed chemistry of heavy-ion-induced degradation. We report here the results of our first experiments in this regard done at the newly installed M-branch of UNILAC accelerator, GSI. Commercially-available 25 m-thick PVDF films were irradiated at room temperature by 4.8 MeV/u U at fluencies of up to 610 ions/cm. This irradiation was performed in the multi-purpose chamber of the M3 beamline equipped with a Fourier-transform infrared (FT-IR) transmission spectrometer as well as a residual gas analyzer. When irradiated at a fluence of 110 ions/cm, the film showed three new absorption bands, which can be identified as in-chain and chain-end unsaturations in the PVDF main chain. According to the analysis of outgassing fragments, hydrogen fluoride can be predicted as degradation product for the formation of these unsaturated bonds.
Yamaki, Tetsuya; Nuryanthi, N.*; Koshikawa, Hiroshi; Sawada, Shinichi; Hakoda, Teruyuki; Asano, Masaharu; Maekawa, Yasunari; Voss, K.-O.*; Severin, D.*; Seidl, T.*; et al.
no journal, ,
We examined chemical structures of the defects in an ion track penetrating through poly(vinylidene fluoride) (PVDF), and accordingly, presented a pretreatment technique for achieving more efficient track etching. A 25 m-thick PVDF film was bombarded with 1.1 GeV U or 450 MeV Xe ions. According to the infra-red spectroscopy and residual gas analysis, the formation of many double bonds were found to occur in the PVDF main chain with the evolution of hydrogen fluoride. The knowledge of the solubility in a permanganate alkaline solution and our preliminary experiment suggested the importance of oxidized tracks for the easy introduction of the etching agent. We finally found that the pretreatment with ozone could oxidize the double bonds in the tracks, thereby vigorously promoting track etching before breakthrough.
Yamaki, Tetsuya; Koshikawa, Hiroshi; Asano, Masaharu; Maekawa, Yasunari; Severin, D.*; Seidl, T.*; Trautmann, C.*
no journal, ,
We irradiated a poly(vinylidene fluoride) (PVDF) film with swift heavy ions, and then examined chemical structures of the defects created in the resulting track. The 25 m-thick PVDF film was bombarded with 1.1 GeV U ions in the multi-purpose chamber, where degradation processes were monitored by FT-IR spectroscopy and residual gas analysis as a function of the fluence. At fluences above 1.010 ions/cm, the film showed two new absorption bands identified as double-bond stretching vibrations of in-chain unsaturations and fluorinated vinyl groups. These defects would result from the evolution of HF, which was seen in the residual gas analysis and would be explained by a four-center mechanism.
Yamaki, Tetsuya; Nuryanthi, N.*; Koshikawa, Hiroshi; Asano, Masaharu; Sawada, Shinichi; Hakoda, Teruyuki; Maekawa, Yasunari; Voss, K.-O.*; Severin, D.*; Seidl, T.*; et al.
no journal, ,
The possibility of varying the beam parameters and applying the effect of a pre-etching treatment for poly(vinylidene fluoride) (PVDF) ion-track membranes was investigated with the goal of achieving enhanced track etching for effective control of the pore size and shape. Commercially available 25 m-thick PVDF films were irradiated at room temperature with swift heavy ions. Irradiation with a higher-LET beam gave faster track etching and larger pores, suggesting that the LET could be the most crucial factor determining the pore size. In-situ infra-red absorption and residual gas analyses shed light on the detailed chemistry of not only the ion-induced degradation, but also post-irradiation reactions. The pre-etching treatment effect involved oxidation of the unsaturated bonds within the latent track, which accelerated the chemical dissolution for efficient pore evolution. In other words, exposure to a gaseous oxidant, i.e., ozone, shortened the breakthrough time.
Yamaki, Tetsuya; Nuryanthi, N.*; Koshikawa, Hiroshi; Asano, Masaharu*; Sawada, Shinichi; Kitamura, Akane; Maekawa, Yasunari; Kay-Obbe, V.*; Severin, D.*; Seidl, T.*; et al.
no journal, ,
Practically, polyvinylidene fluoride (PVDF) has been said to be the only fluoropolymer in which ion tracks can be developed by chemical etching. We thus investigated the possibility of varying the beam parameters and applying the effect of a pre-etching treatment for PVDF ion-track membranes with the goal of achieving enhanced track etching for effective control of the pore size and shape. Our activities also cover all types of fluoropolymers including PVDF. Compared to PVDF, poly(ethylene--tetrafluoroethylene) and a series of perfluoropolymers are known to be very stable in highly-concentrated acid or alkaline solutions or at higher temperatures. Although this property might make their ion-track etching very challenging, the ongoing research is expected to allow one to accumulate know-how on methods of chemical etching, which can be generalized for the chemical structures. These will give feedback to a guiding principle for effective ion-track etching in fluoropolymers.