Characterization of iron-based and tungsten-based high-entropy alloys

Wakai, Eiichi; Noto, Hiroyuki*; Shibayama, Tamaki*; Iwamoto, Yosuke; Sato, Koichi*; Yano, Yukihiro*; Yoshikawa, Maya*; Nakagawa, Yuki*; Toyota, Kodai; Onizawa, Takashi

no journal, , 

In this study, we attempted to fabricate Fe-based and W-based Fe-HEA and W-HEA, both of which have been studied extensively in recent years to enhance the durability of equipment used in high-energy beam irradiation environments. For Fe-based HEAs, Fe-Mn-Cr-V-Al-C alloys were melted and casted, and then subjected to homogenization heat treatment (homogenization heat treatment (1150C for 2h)). After homogenization heat treatment, a 3-point bending test was performed at room temperature. The homogenization heat treatment resulted in an increase in ductility in the 3-point bending test and a decrease in elastic modulus based on ultrasonic velocity measurements. XRD measurements of this material after heat treatment (800C for 10 min and Water Quenched) showed that it has a BCC structure and a Vickers hardness that exceeds that of pure W. On the other hand, in the preparation of W-based HEA material (W-Fe-Si-V-Cr alloy), an arc melting method using powder was attempted, and it was found that an almost homogeneous crystallized alloy could be produced.