Yamamoto, Masahiro; Sato, Tomonori; Komatsu, Atsushi; Nakano, Junichi; Ueno, Fumiyoshi
Proceedings of European Corrosion Congress 2015 (EUROCORR 2015) (USB Flash Drive), 7 Pages, 2015/09
In Fukushima-Daiichi Nuclear Power Station, decommissioning procedures are continuing and it will take more than 30 years. As some structures are made of carbon steel, degradation by corrosion is large problem for structural reliability. To clarify an irradiation effect for corrosion of carbon steel, corrosion test was con-ducted in Co
-ray irradiated condition. Corrosion test results showed that corrosion rates of
-ray irradiated condition increased with
-ray dose rates. The oxidant concentrations were also increased with
-ray dose rate. From these results, a new estimation method for corrosion rate of carbon steel in water with
-ray irradiated condition using radiolysis calculation is introduced and discussed.