The Evaluation of the influence of hydride rim and biaxial stress condition on the cladding failure under a reactivity-initiated-accident by using EDC test method

Shinozaki, Takashi; Mihara, Takeshi; Udagawa, Yutaka; Sugiyama, Tomoyuki; Amaya, Masaki

JAEA-Research 2014-025, 34 Pages, 2014/12

JAEA-Research-2014-025.pdf:6.05MB

EDC test is a test method on the mechanical property of fuel cladding tube, and it focuses on the stress condition generated by PCMI under a RIA. We conducted EDC tests which simulate the mechanical conditions during a RIA by using the unirradiated cladding tubes which simulate hydride rim. Circumferential residual strains observed in post-test specimens tended to decrease with increasing the hydrogen concentration in the test cladding tubes and the thickness of the hydride rim. We also prepared RAG tube and performed EDC tests on it. It was observed that circumferential total strains at failure tended to decrease with increasing pre-crack depth on the outer surface of RAG tube specimen. We conducted biaxial stress tests by applying longitudinal tensile load onto RAG tube specimens. It was observed that circumferential total strains at failure under biaxial stress conditions tended to decrease compared to the results under uniaxial tensile condition.