Ezato, Koichiro; Suzuki, Satoshi; Seki, Yohji; Mori, Kensuke; Yokoyama, Kenji; Escourbiac, F.*; Hirai, Takeshi*; Kuznetsov, V.*
Fusion Engineering and Design, 98-99, p.1281 - 1284, 2015/10
Times Cited Count：47 Percentile：96.35(Nuclear Science & Technology)Japan Atomic Energy Agency (JAEA) is now devoting to development of Full-W ITER divertor outer vertical target (OVT), especially, PFU that needs to withstand the repetitive heat load as high as 20MW/m
. JAEA have succeeded in demonstrating that the soundness of a bonding technology is sufficient for the full-W ITER divertor. For the development of bonding technology, the load carrying capability test on the W monoblock with a leg attachment to an OVT support structure was carried out and shows that the attachment can withstand against the uniaxial load more than 20 kN which is three times higher than the IO requirement. JAEA manufactured 6 small-scale mock-ups and tested under the repetitive heat load of 10 and 20 MW/m to examine the durability of the divertor structure including W tile bonding and the cooling tube. All of the mock-ups could survived 5000 cycles at 10 MW/m and 1000 cycles 20 MW/m with no failure such as debonding of the W tile and water leak from the cooling tube. The number of cycles at 20 MW/m is three times longer than the requirement of ITER divertor.
Teshigawara, Makoto; Harada, Masahide; Saito, Shigeru; Kikuchi, Kenji; Kogawa, Hiroyuki; Ikeda, Yujiro; Kawai, Masayoshi*; Kurishita, Hiroaki*; Konashi, Kenji*
Journal of Nuclear Materials, 343(1-3), p.154 - 162, 2005/08
Times Cited Count：10 Percentile：55.76(Materials Science, Multidisciplinary)For decoupled and poisoned moderator, a thermal neutron absorber, i.e., decoupler, is located around the moderator to give neutron beam with a short decay time. A B4C decoupler is already utilized, however, it is difficult to use in a MW class source because of He void swelling and local heating by (n,a) reaction. Therefore, a Ag-In-Cd (AIC) alloy which gives energy-dependence of macroscopic neutron cross section like that of B
C was chosen. However, from heat removal and corrosion protection points of view, AIC is needed to bond between an Al alloy (A6061-T6), which is the structural material of a moderator. An AIC plate is divided into a Ag-In (15wt%) and Ag-Cd (35wt%) plate to extend the life time, shorten by burn up of Cd. We performed bonding tests by HIP (Hot Isostatic Pressing). We found out that a better HIP condition was holding at 803 K, 100 MPa for 1 h for small test pieces (f20mm). Though a hardened layer is found in the bonding layer, the rupture strength of the bonding layer is more than 20 MPa, which is less than that of the design stress.
Hatano, Toshihisa; Enoeda, Mikio; Kuroda, Toshimasa*; Akiba, Masato
JAERI-Tech 2002-075, 59 Pages, 2002/10
JAERI-Tech-2002-075.pdf:17.38MB
no abstracts in English
Sato, Satoshi; Takatsu, Hideyuki; Hashimoto, T.*; Kurasawa, Toshimasa; Furuya, Kazuyuki; ; Osaki, Toshio*; Kuroda, Toshimasa*
Journal of Nuclear Materials, 233-237(PT.B), p.940 - 944, 1996/00
Times Cited Count：34 Percentile：91.73(Materials Science, Multidisciplinary)no abstracts in English