Wang, Y.*; 友田 陽*; 大村 孝仁*; Gong, W.; Harjo, S.
Materialia, 27, p.101685_1 - 101685_9, 2023/03
The evolution of internal stress during displacive transformation is a topic of continuous debate. Neutron diffraction was used to study the isothermal bainite transformation in a 0.4 C low alloyed steel from 773 to 623 K to provide a clearer basis for discussion regarding the change in the austenite lattice parameter. According to diffraction profile analysis, fresh bainite possesses a body-centered tetragonal structure, and its c/a ratio decreases rapidly over time. The austenite lattice parameter increases or decreases depending on whether the transformation temperature is above or below the nose of the Time-Temperature-Transformation (TTT) curve. This isothermal transformation behavior can be divided into two categories: above and below the nose of TTT curve, which correspond to the upper and lower bainites, respectively. The internal stresses caused by the transformation strains are relaxed by dislocation motion and vacancy formation. The yielded dislocations and vacancies not only affect the broadening of both austenite and bainitic ferrite diffraction peaks but also the lattice parameter.
飯田 國廣*; 柴田 勝之; 植田 脩三; 小林 英男*; 樋口 洵*; 高允 宝*; 片田 康行*; 深倉 寿一*; 笠井 憲一*; 仲尾 元六*; et al.
JAERI-M 91-224, 88 Pages, 1992/01
本報告書は、原研が構造機器の疲労寿命評価に関連した委託研究および構造材料の経年変化に関連した委託研究において取得した成果のうち、原子力材料の低サイクル疲労試験結果をデータ集として取りまとめたものである。掲載したデータは、原研が委託調査により開発した疲労データベースFADALを検索して、表形式および
-Nf線図として記載した。
庄子 哲雄*; 中島 甫; 近藤 達男; 高橋 秀明*
材料, 31(346), p.703 - 709, 1982/00
腐食疲労き裂成長速度に及ぼす種々の力学的因子の役割を割れ成長の機構にもとづいて統一的に評価することを試み、き裂先端におけるひずみ速度の重要性を指摘した。さらに、このき裂先端のひずみ速度は時間基準のき裂成長速度(da/dt|air)、によって評価されることを示し、軽水炉圧力境界壁材の高温水中における割れ成長速度データを用いてその妥当性を検証した。SSRT試験(低速度引張試験)結果も同じ手法によって整理されることを示し、da/dt|air-da/dt|cenirronment線図によるき裂成長速度の評価、予測がさらに一般的な負荷様式にまで拡張され得る事を示した。